温度对不锈钢经电浆软氮化後之影响.doc

40BCrV鋼熱處理硬度不均之改善 The Improvement of Hardness Uniformity After Heat Treatment for 40BCrV Steel 張恆碩* 郭瑩澤** Herng-Shuoh Jang* Ying-Che Kuo** *中鋼公司-鋼鐵研究發展處-鋼鐵產品開發組 **冶金技術處-冶金技術服務組 摘要 …之生產製造。這些手工具用鋼料若沒有透過適當的熱處理，便容易產製出硬度不均，特性不佳的產品，無法滿足客戶之需求。其中40BCrV鋼更是為國內棘輪扳手製造業者所常使用之鋼料，由於有業者反應產品在熱處理後容易發生硬度不均，疲勞壽命不足的現象，因此在中鋼的熱處理協助下，該業者之X規格棘輪扳手、其硬度滿足HRC50，扭力值符合DIN要求值512N·m之1.5倍(768N·m)以上，且在DIN要求值之扭力值1/4(128N·m)水平下施以疲勞壽命測試，疲勞壽命滿足5萬次以上之測試水準。 關鍵字： Abstract The Chromium-Vanadium Steel is commonly used for hand tools, such as bits, wrentches, sockets...etc. If these hand tool steels were not subjected to proper heat treatment, it would be facilitaed to produce non-uniform and worse property products. Hence, that is unable to meet the demands of customers. For these hand tool steels, 40BCrV steel is the most popular steel used in ratchet wrench manufacturing for domestic manufacturers. One of the users responsed that some products after heat treatment prone to uneven hardness and insufficient fatigue life. Under the assists of China steel corp. (CSC), the required properties for the customers X type ratchet wrench meet the demands : the hardness must be greater than HRC50 and the torque value must be greater than 768 N·m under 1.5 times DIN specification demanded value 512 N·m and the fatigue life must be greater than 50 thousand times under the torque value 128 N·m demanded on 1/4 times DIN specification requirement value 768 N·m. 1. 前 言…之生產製造。由於國際手工具大廠對於產品特性之需求相當嚴苛，再好的鋼料若沒有透過適當的熱處理，往往容易產製出硬度不均，特性不佳的產品，以致無法滿足客戶之需求。其中40BCrV鋼更是為國內棘輪扳手製造業者所常使用之鋼料。 由於有業者向中鋼反應，其產品採中鋼40BCrV鋼在加工及委外熱處理後，常發生硬度不均，疲勞壽命不足的現象。因此，客戶希望中鋼能協助其熱處理，並取得熱處理製程參數，以利將來將熱處理作業移回其廠內加工施行。為了落實中鋼高層推動2.5級產業之理念，希望將服務理念深耕融於製造業，透過服務加值使中鋼下游客戶的產品能更臻完美，因此希望由中鋼的熱處理協助下，該業者之X規格H柄棘輪扳手、產品硬度滿足HRC50，扭力值符合DIN要求值512N·m之1.5倍(768N·m)以上，且在DIN要求值之扭力值1/4(128N·m)水平下施以疲勞壽命測試，疲勞壽命滿足5萬次以上之測試水準。 2. 實驗方法 2.1 圖1 熱鍛退火材經研磨壓平之粗胚試棒 由於此次客戶之需求，主要為產品熱處理後硬度不均，且疲勞壽命不穩定，因此由中鋼向客戶索取50支“熱鍛退火+研磨軋平”材[簡化稱“熱鍛退火”材]，於中鋼實驗室展開熱處理調質試驗。 熱處理之取材，主要採兩種起始材進行展開：一種為直接採“熱鍛