红土镍矿堆浸试验.doc

红土镍矿堆浸试验 童伟锋，汪云华，吴晓峰，范兴祥 （昆明贵金属研究所 稀贵金属综合利用新技术国家重点试验室，昆明 650106） 摘要：对澳大利亚红土镍矿进行两段逆流堆浸。考察了矿样粒度、浸出液酸浓度、浸出时间、堆高对镍浸出率的影响。结果表明使用粒度为2~8 mm的矿样，一段浸出使用二段浸出液，堆浸时间16天；二段浸出使用新配置的酸液浸一段浸出渣，酸浓度为22%，堆浸时间6070天，整个流程镍浸出率为80.28%。 关键词：镍红土镍矿堆浸Experimental Study on Heap Leaching of Nickel Laterite TONG Wei-feng,WANG Yun-hua,WU Xiao-feng, FAN Xing-xiang （Kunming Institute of Precious MetalsState Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Kunming 650106, China） Abstract: n Australian nickel laterite ore was heap leached with the two stage countercurrent process. The effects of particle size, acid concentration, leaching time, and heap high on nickel leaching rate were investigated. The results show that the nickel leaching rate is up to 80.28% in the whole process. In the first stage, the ore with particle size of 2~8 mm is leached for 16 days with second stage leaching lixivium, and in the second stage, the first leaching residue is heap leached for 60 to 70 days with the sulfuric acid concentration of 22%. Key words: nickel; nickel laterite; heap leaching 据估计，镍在地壳中的平均含量为0.01%，而红土镍矿则占了世界镍储量的70%1]。红土镍矿是由铁和镍的氧化物组成的次生共生矿，其特点是硬度小、易泥化、含水高（3045%）、难于用一般选矿方法富集品位约1%3%[2]。因此，红土镍矿将会成为未来镍的主要来源，受到众多研究者的关注。 目前，红土镍矿的冶炼方法分为火法和湿法两大类。火法主要有还原熔炼生产镍铁工艺3-6]、还原硫化熔炼生产镍锍工艺；湿法处理红土镍矿的方法主要为还原焙烧氨浸工艺、加压硫酸浸出工艺、常压硫酸浸出工艺13]。其中，常压硫酸浸出工艺具有工艺简单、能耗低、不使用高压釜、投资费用少、操作条件易于控制等优点越来越受到人们的关注常压硫酸浸出又分为堆浸、泡浸和搅拌浸出。为充分利用硫酸并提高镍的浸出率，本文采用堆浸法对澳大利亚红土镍矿进行两段逆流浸出，考察工艺条件对镍浸出效果的影响。 试验原料及方法 .1 试验原料 红土镍矿澳大利亚GME公司，矿样经晾晒、自然干燥，破碎后筛分为2 mm、mm、mm和225 mm四个粒级，各粒级的化学成分见表1。 表1 红土镍矿各粒级化学成分 Table 1 hemical composition of nickel laterite with different grain size /% 粒度/mm Ni Co Fe Mg -21.14 0.13 21.09 2.62 2~8 1.04 0.12 20.83 2.40 2~15 1.06 0.10 19.87 2.50 2~25 1.15 0.13 20.16 2.67 由表1可知，该红土镍矿中各粒级矿样的化学组成非常相近，属于低镍高铁低镁的铁质镍矿石，适于采用湿法提取工艺。 基金项目：国家科研院所技术开发专项资金（NCSTE-2007-JKZX-062）；云南省科技计划项目（2008AA001） 收稿日期：2011-12-05 作者简介：童伟锋（1979-），男，上海市人，大学，助理工程师. 1.2 试验设备与试剂 试验中使用的设备主要为15个浸取柱1.5 m、2.2 m和3 m的各3个，0.20 m