PRODUCT SPECIFICATION (BUHIA SUL) PULP BALES Method Min Max Gross weight, kg 250 Brightness, %, ISO ISO2470 88.9 - Dimensions, cm 67?2?5 Intrinsic Viscosity, dm3/kg SCAN C15 700 - Wires Number 3 Dirt Count, mm2/kg ISO5350 - 2.0 Diameter, mm 2.18 Moisture, % (*) 8 12 ONE UNIT=8 Bales=2,000 kg (*)Bahia Sul’s method specific for Scampro Celluref CR-20T equipment TYPICAL TEST RESULTS Properties Method STD PULP ECF PULP OPTICL: Brightness, %, ISO ISO2470 89.6 89.4 Brightness Reversion, NCP TAPPI T-269 0.37 0.36 Color Coordinates C.I.E. L ELREPHO 97.3 97.3 a ELREPHO -0.545 -0.594 b ELREPHO 3.183 3.183 CHEMICAL Pentosan Content, % (**) 16.0 15.9 D.C.M Extractives, % SOXTEC-HT 1043 0.15 0.13 Ash Content, ppm SCAN-C 6 2846 3002 A.O.X., ppm PTS-RH11 31 15 PHISICAL-CHEMICAL Intrinsic Viscosity, dm3/kg SCAN-C15 811 820 Pulp PH ISO6588 5.7 5.5 IONS CONTENT Calcium, ppm SCAN-C10 369 507 Sodium, ppm SCAN-C30 480 487 Iron, ppm SCAN-CM13 15 14 ANATOMICAL Fiber Length, mm KAJAANI 0.76 0.75 Fiber Coarseness, mg/100m FS 9.0 9.1 Number of Fibers per Gram (million) 200 18.0 17.9 Volume, ml (2% consistency) SEDIMENT 1362 1402 (**)Browning, B.L.-Methods of Wood Chemistry, New York, 1967. 882p  TYPICAL DISC REFINER RESPONSE – ECF STANDARD PULPS Typical Pulp Properties Values TARGET VALUE FOR TENSILE INDEX 25Nm/g 30Nm/g 35Nm/g 40 m/g 45Nm/g 50 Nm/g 55Nm/g Slowness, 癝R 23.1 25.5-26.3 30.1-31.2 36.3-38.9 44.1-48.6 53.3-60.51 54.2-74.6 Apparent Density, kg/m3 515 535 556 5 76 597 618 639 Bulk, cm3/g 1.942 1.869 1.799 1.736 1.675 1.618 1.565 Tear Index, Nm2/kg 4.19 4.96 5.74 6.51 7.28 8.06 8.83 Light Scattering Coefficient, m2/kg 44.7 43.7 42.9 42.1 41.4 40.8 40.3 Gurley Air Resistance, sec/100 ml 0.954 0.909 1.304 1.871 2.518 3.275 4.14 Net Refining Energy, kWh/t Refining at 0.5 ws/m (*) - 21.6 36.4 51.1 65.9 80.7 95.5 Refining at 1.0 ws/m (*) - 29.6 54.1 78.7 103.3 127.8 152.4 Refining at 1.5 ws/m (*) - 42.7 79.1 115.5 151.9 188.2 224.6