リン系難燃剤で処理された木材の遮熱性.pdfVIP

－研究－ リン系難燃剤で処理された木材の遮熱性 菊地 伸一 駒澤 克己 Thermal Insulation Property of Laminated Timbers Treated with Phosphorous Fire Retardant Shin’ichi KIKUCHI Katsumi KOMAZAWA The internal temperature and thermal insulation have been measured for laminated timbers of spruce and Yellow poplar treated with phosphorous fire retardant，and compared with data for untreated wood．The wood thickness was 15 to 30mm，and the fire retardant retention was 160～190kg/m3．The samples were exposed in a furnace fo1lowing the JIS A 1304 time-temperature curve．The thermal insulation properties of laminated timbers were evaluated by the times needed for the back side temperature go up to 260℃． The thermal insulation property was increased with the thickness of the timber．When the thickness of laminated timbers was thin，fire retardant treatment was very efftctive on the thermal insulation and it was found to increase the mean thermal insulation about 40％． Keywords ：fire retardant，fire proof property，internal temperature，thermal insulation，charlayer 難燃剤，耐火性能，内部温度，遮熱性，炭化層 リン系難燃剤で処理されたスプルース，イエローポプラの集成材を耐火加熱し，内部温度および遮 熱性能について検討した。供試体の厚さは15～30mm，難燃剤含量は160～190kg/m3 とした。供試 体はJIS A 1304の温度曲線に沿って加熱し，遮熱性能は裏面温度が260℃に達するまでの時間で評 価した。 木材が厚くなるほど遮熱性は向上した。難燃処理による遮熱性向上効果は板の厚さが薄い場合に大 きくあらわれ，遮熱性は平均で40％程度大きくなった。 1．はじめに 題となる。木造建築物の火災時における構造安全性 木材の難燃化は，内装材料をその主要な対象とし は，主に集成材を利用した大規模建築物について検 て実施されており，着火性，発熱性，および火炎伝 討されており，加熱による強度変化1-4)，炭化速度5-8) 播性などの表面燃焼性の抑制を目的としている。こ などが明らかにされている。また，集成材のような れは，内装材料の着火を防止し発熱速度を低減させ 大断面木材以外でも，木製防火ドアや準耐火構造で ることが初期火災の拡大防止に効果的で，安全性を は木材の表面が燃焼した後に生じる炭化層を，裏面 確保することにつながるからである。 への熱伝導を低下させる断熱層として利用してい 一方，フラッシュオ