瓦楞纸板承载能力疲劳损伤曲线研究.pdfVIP

编号：B06 瓦楞纸板承载能力疲劳损伤曲线研究 孙聚杰 （青岛科技大学橡塑材料与工程教育部重点实验室，青岛266042 ） 摘要：瓦楞纸板在使用的过程中，随着振动、冲击次数的增加，其性能会不同程度的衰减下降，出现疲劳现象。对A 型瓦楞纸板进行疲劳振动试验，通过试验获得瓦楞纸板不同振动加速度下的疲劳损伤次数，得出疲劳破损曲线N-A ， 并进行了两级应力振动疲劳累积效应分析，为瓦楞纸板承载功能的实现提供有价值的参考。 关键词：瓦楞纸板，疲劳，振动，疲劳破损曲线，加速试验 Research on Fatigue Damage Curve of Load Capacity of Corrugated Fiberboar SUN Jujie (Key Laboratory of Rubber-plastics (Qingdao University of Science and Technology), Ministry of Education,Qingdao 266042; China) Abstract:The performance of corrugated fiberdboard may be weaken drop,in the use process, along with the vibration, the impact number of times increase, and appear the fatigue phenomenon. The fatigue vibration test of corrugated fiberboard was conducted. The damage number of vibration and vibration acceleration w as determined,get the damage curve N-A . And carried on two level of stress vibration fatigue cumulative effect analysis,in order to meet the anticipated packaging effect. Key words: corrugated fiberboard; fatigue; vibration; fatigue damage curve; acceleration test 振动与冲击是导致产品破损的主要原因。产品流通中振动破损主要有两种形式：一是共振条件 下共振加速度超过极限值而发生的破损；二是非共振条件下，由于包装材料的疲劳损伤，降低了对 [1] 被包装物的防护功能 。 [2-5] 缓冲包装材料种类繁多，现阶段对于缓冲材料的研究，主要集中在材料初始缓冲性能 和本构 [6-8] 模型方面 ，同时现行的材料缓冲性能的测试方法也只局限于对材料的前五次压缩、跌落试验进行 [9] 分析计算 。实际包装产品在流通过程中，经历的振动冲击次数往往达到几万次甚至更多，作为起 保护产品作用的缓冲材料，也随之发生了相应的压缩、复原，即发生疲劳效应，其缓冲性能将发生 相应的变化，特别是对于常用的纸板类材料，疲劳强度对其性能的影响将尤为显著。孙聚杰、卢立 [10] 新研究了疲劳压缩对瓦楞纸板性能的影响 和不同振动次数后的瓦楞纸板承载能力和静态缓冲系数 的变化情况[11、12] 。至今还未发现有其他相关文献对缓冲材料进行疲劳性能方面的研究。 1 瓦楞纸板疲劳失效形式 对于在循环荷载下工作的瓦楞纸板来说，疲劳是一种重要的极限状态，长时间的循环载荷作用 对剩余强度、韧性和弹性响应都有不利影响，所以无论是承载力的下降，还是弹性模量的下降都应 该得到重视