碳纤维织物增强混凝土薄板弯曲性能试验研究.pdfVIP

碳纤维织物增强混凝土薄板弯曲性能试验研究 佘斌 荀勇 李玉寿 余雄明 （盐城工学院 盐城224053） 摘 要：采用两组碳纤维织物增强混凝土薄板，其中一组给碳纤维织物施加一个 预应力，另一组不加预应力，在电子式万能试验机上进行四点弯曲试验，利用 dataTaker DT515数据采集仪进行同步自动采集荷载、位移和应变数据，分析了 两组试件在不同剪跨比下的裂缝情况，及荷载—位移曲线、荷载—应变曲线特征。 试验结果表明：对碳纤维织物施加预应力后，碳纤维织物增强混凝土薄板的开裂 荷载提高，抗弯性能增强，破坏时变形减少。 关键词：碳纤维织物 混凝土薄板 抗弯性能 试验研究 Experimental study on bending performance of carbon textile reinforced concrete sheets Shebin Xunyong Liyushou Yuxiongming Abstract: Using two types of carbon textile reinforced concrete sheets, prestressed and non-prestressed, the four-point bending tests were carried out on the electronic universal testing machine. The data of load ，displacement and strain were collected automatically by dataTaker DT515. The crack condition of the two types of specimens with different shear span ratio was analyzed, and the characteristics of load-displacement and load-strain were also analyzed. The experimental results indicate that, comparing with the non-prestressed textile reinforced concrete sheets, the concrete sheets reinforced with prestressed carbon textile have higher initial cracking load, better flexural performance and smaller failure deformation. Keywords: carbon textile; concrete sheet; flexural performance; experimental study 1 引言 织物增强混凝土薄板的研究是纤维增强混凝土研究中重要方面之一，用于增强混凝土的 织物产品主要是指用耐碱玻璃纤维粗纱或碳纤维粗纱等通过纺织技术织造而成的网状产品， 其中经纬向双层缝编织物的应用较为广泛。碳纤维以其非常高的弹性模量和强度而闻名，通 常它的强度高于高质量的预应力钢。在结构加固方面，这种高强度的性能是特别受欢迎的， 而碳纤维的高强度，在没有预应力的情况下，通常不能发挥作用。 预应力织物增强混凝土薄板的研究工作在全球内才刚刚起步，在国内该领域还处于空白 第 435 页 状态，织物增强混凝土的研究是该领域的重要方面之一，预应力织物增强混凝土薄板的研究 是织物增强混凝土薄板研究的进步和深入，它不同于碳纤维布加固混凝土结构研究领域。采 用高性能织物增强混凝土制作薄板时，采用预拉伸织物使混凝土在受荷前先受压的方法，能 够更好地发挥高性能织物的作用，提高了薄板的抗裂性能和抗渗性能，有效的阻止了腐蚀性 气体和液体渗过薄板，因此可以认为预应力织物增强混凝土薄板比非预应力增强混凝土薄板 更加先进。 2 试验概况 弯曲试验所用试