Explosive shock processing of Pr2Fe14B-Fe
Explosive shock processing of Pr2Fe14B/–Fe
exchange-coupled nanocomposite bulk magnets
Z.Q. Jin
School of Materials Science and Engineering, Georgia Institute of Technology,
Atlanta, Georgia 30332; and Department of Physics, University of Texas at Arlington,
Arlington, Texas 76019
N.N. Thadhani,a) M. McGill, Y. Ding, and Z.L. Wang
School of Materials Science and Engineering, Georgia Institute of Technology,
Atlanta, Georgia 30332
M. Chen and H. Zeng
IBM T.J. Watson Research Center, Yorktown Heights, New York 10598; and Department of Physics,
University of Texas at Arlington, Arlington, Texas 76019
V.M. Chakka and J.P. Liu
Department of Physics, University of Texas at Arlington, Arlington, Texas 76019
(Received 31 August 2004; accepted 26 October 2004)
Explosive shock compaction was used to consolidate powders obtained from melt-spun
Pr2Fe14B/–Fe nanocomposite ribbons, to produce fully dense cylindrical compacts of
17–41-mm diameter and 120-mm length. Characterization of the compacts revealed
refinement of the nanocomposite structure, with approximately 15 nm uniformly sized
grains. The compact produced at a shock pressure of approximately 1 GPa maintained
a high coercivity, and its remanent magnetization and maximum energy product were
measured to be 0.98 T and 142 kJ/m3, respectively. The compact produced at 4–7 GPa
showed a decrease in magnetic properties while that made at 12 GPa showed a
magnetic softening behavior. However, in both of these cases, a smooth hysteresis loop
implying exchange coupling and a coercivity of 533 kA/m were fully recovered after
heat treatment. The results illustrate that the explosive compaction followed by
post-shock heat treatment can be used to fabricate exchange-coupled nanocomposite
bulk magnets with optimized magnetic properties.
I. INTRODUCTION
A variety of nanocomposites consisting of hard mag-
netic R2Fe14B (R rare earth) and soft magnetic –Fe
or Fe3B phases are being extensively investigated due
to their potentially high
您可能关注的文档
- Discrete Element Method Simulation of Cylinder-Shaped Particle Flow in a Gas-Solid Fluidized Bed.pdf
- Discrete quasiperiodic sets with predefined covering cluster.pdf
- Discrete-Time Sliding Mode Observer for.pdf
- Discussion of Least angle regression by Efron et al.pdf
- Discretized opinion dynamics of Deffuant on scale-free networks.pdf
- Disease Presentation 1.pdf
- Dislocation constriction and cross-slip in Al and Ag an ab initio study.pdf
- Dispersible Surface-Enhanced Raman Scattering Nanosheets(.2012 Adv. Mater).pdf
- Dissolution kinetics of delta ferrite in AISI 304 stainless steel produced by strip casting process.pdf
- Distance matrix completion by numerical optimization.pdf
文档评论(0)