GH696合金高温变形过程中的塑性变形行为.pdfVIP

Trans. Nonferrous Met. Soc. China 26(2016) 712−721 Plastic flow behavior of superalloy GH696 during hot deformation Zhao-hua XU, Miao-quan LI, Hong LI School of Materials Science and Engineering, Northwestern Polytechnical University, Xi’an 710072, China Received 23 March 2015; accepted 20 October 2015 Abstract: In order to investigate the hot deformation behavior of superalloy GH696, isothermal compression experiments were − 1 carried out at deformation temperatures of 880− 1120 °C and strain rates of 0.01− 10 s . And the deformation amount of all the samples was 50%. The strain rate sensitivity exponent (m) and strain hardening exponent (n) under different deformation conditions were calculated, meanwhile the effects of the processing parameters on the values of m and n were analyzed. The results show that the flow stress increases with the increase of strain rate and the decrease of deformation temperature. The value of m increases with the increase of deformation temperature and decreases with the increase of strain rate, while the value of n decreases with the increase of deformation temperature. A novel flow stress model during hot deformation of superalloy GH696 was also established. And the calculated flow stress of the alloy is in good agreement with the experimental one. Key words: superalloy GH696; flow stress; deformation behavior; strain rate sensitivity exponent; strain hardening exponent; flow stress model superalloy GH696, in which a model for peak stress and 1 Introduction processin