宝钢IF钢的生产工艺与改进建议.doc

宝钢IF钢的生产工艺与改进建议 马衍伟　王先进　孔冰玉 　(北京科技大学)　　(宝山钢铁(集团)公司) 摘　要　在对宝钢现有装备条件、生产工艺技术以及IF钢产品质量深入调研的基础上，较全面地分析了影响IF钢力学性能与成型性能的工艺因素；讨论了各个工艺环节间的有机联系。据此对宝钢提出了稳定IF钢产品质量的建议。关键词　IF钢　生产工艺　成型性能 PRODUCTION TECHNOLOGY OF IF STEEL AT BAOSTEEL ANDSUGGESTIONS FOR QUALITY IMPROVEMENT MA Yanwei　WANG Xianjin (University of Science and Technology Beijing) KONG Bingyu (Baoshan Iron and Steel Corp.) ABSTRACT　Recently,IF steel sheets of Baosteel have been used by many domestic automotive factories,however,the production scale is small and the properties sometimes fluctuate.So the effect of technological factors on mechanical properties and formability of IF steel have been investigated based on existing equipment,process technology at Baosteel.Suggestions for improving IF steel are proposed.KEY WORDS　IF steel,production technology,mechanical properties 1　前言 　　80年代以来，随着冶金生产技术的进步和汽车工业的发展，IF钢得到迅速发展。1997年仅日本IF钢的年产量就超过1　000万t。以IF钢为基础发展起来的深冲热镀锌IF钢板、深冲高强度IF钢板、深冲高强度烘烤硬化(BH)IF钢板等系列，已形成了第三代汽车冲压用钢。IF钢的生产已经成为一个国家汽车用钢板的标志。降低生产成本并开发物美价廉的品种是目前IF钢研究和生产的趋势。　　我国研制IF钢始于1989年，北京科技大学与宝钢合作，在没有引进外国专利的情况下，用了不到二年的时间基本完成了IF钢的开发，填补了国内空白。1995年宝钢IF钢产量为6万多吨，1996年达8.4万t。但是和国外钢厂相比，其成材率较低。为此进行了IF钢大生产数据的收集和分析，为优化工艺路线提供依据。 2　IF钢生产工艺要点 　　IF钢的生产工艺流程为转炉冶炼—RH真空脱气—连铸—热轧—冷轧—退火—平整。生产过程的每一步工序，从成分控制到热轧、冷轧、退火、平整都影响IF钢的最终性能。为了获得优异的深冲性能，下述三个因素最为关键：　　(1) 发展强的(111)退火织构，以获得高的深冲性()；　　(2) 获???足够粗大均匀的铁素体晶粒，以获得低的σs/σb和高的加工硬化指数(n)；　　(3) 控制第二相粒子(碳、氮化物)的析出，以控制时效效应，改善塑性。　　故IF钢的生产应命中①非时效性；②强的(111)再结晶织构；③较粗大的铁素体晶粒等三个目标，如表1所示［1］。冶炼中应尽可能降低C、N及非金属夹杂(O、S、P)的含量，纯净钢质，一般要求C≤50×10-6，N≤30×10-6，应加入适当的Ti或Nb；热轧宜采用低的板坯加热温度，略大于Ar3的终轧温度，终轧后快速冷却和高温卷曲；冷轧压下率要大；采用尽可能高的退火工艺。上述各个工艺过程对IF钢性能影响的程度也是不同的，按影响程度的大小依次是冶炼，退火，热轧，冷轧。　　目前，宝钢根据冲压性能的不同将IF钢分成BIF1、BIF2、BIF3三个系列。其中BIF1和BIF2为Ti-IF钢(目标成分C≤50×10-6，N≤40×10-6)；BIF3为Nb+Ti-IF钢(目标成分C≤30×10-6，N≤30×10-6)。本文以产量最大的BIF2和BIF3钢为主要论述对象。 表 1　IF钢生产的工艺要点Table 1　Key points of IF steel production 影响程度冶炼　　　→热轧　→冷轧→退火　　技术要点①超低碳②微合金化③钢质纯净①均匀细小的铁素体晶粒②粗大稀疏的二相粒子①尽可能大的冷轧压下率①再结晶晶粒均匀粗大②发展再结晶织构 3　宝钢大工业生产数据统计与分析