Clinical bonding temporary crown zinc oxide eugenol in the clinical experience of adding iodoform.docVIP

 PAGE \* MERGEFORMAT 6 Clinical bonding temporary crown zinc oxide eugenol in the clinical experience of adding iodoform [Keywords:] zinc oxide eugenol iodoform Since 2005-2007 we have the clinical repair treatment, 685 patients were selected temporary crown adhesive, the adhesive in the zinc oxide eugenol iodoform adding some achieved satisfactory clinical results. 1 Materials and methods 1.1 Select a good general condition, outpatient rehabilitation in patients with 685 cases, 423 cases of male and female 262 cases, aged 18 to 55 years. Randomly divided into test group and control group, experimental group of 490 cases, the use of the temporary crown bonded zinc oxide eugenol amount of adhesive added iodoform. the control group 195 patients with normal zinc oxide eugenol cement. 1.2 The correct method of tooth preparation, requiring blunt type prepared shoulder, labial, lingual and mesiodistal tooth preparation in up to normal standards, shoulder height should be in the subgingival 0.3 ~ 0.5 mm. 1.3 tooth preparation is completed, taking alginate infusion plaster model, the model after solidification the excess part of the repair and clear facial, gingival margin may hinder the model is completely in place of gypsum nodules in the preparation and tooth The surrounding area evenly coated with release agent, separating agent to be prepared dry resin temporary crown materials, will be tuned in the model resin temporary crown cover in the prepared tooth, press the anatomy of teeth with a chisel to complete the base appearance. gypsum into a bowl filled with hot water soak for 10 minutes until the resin completely solidified, resin grinding head rubbed off the excess part of the provisional restoration, and further trimmed appearance and gingival margin to reach the base teeth fully in place [1]. 1.4 Provisional restorations in the mouth in place, check the bite with articulating paper. In the estuary in fine-tuning with the grinding point of