生物形态多孔分级结构氧化锡纳米材料的制备研究.docVIP

Hans Journal of Nanotechnology纳米技术, 2011, 1, 22-26 /10.12677/nat.2011.11005 Published Online May 2011 (/journal/nat/) Preparation of Biomorphic Porous Hierarchical SnO Nanomaterials 2 Li Wei , Hui-Lan Su , Fang Song , Won-Jin Moon , Di Zhang 1 1* 1 2 1* State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai 1 2 Korea Basic Science Institute, Gwangju Center, Yongbong-dong, Buk-gu, Gwangju, Republic of Korea Email: hlsu@; venus_wei@163.com Received: Mar.30th, 2011; revised: Apr.26th, 2011; accepted: Apr.29th, 2011. Abstract: In this work, three-dimensional well-organized SnO with porous hierarchy has been successfully 2 synthesized by using pollen grains as the biotemplate and SnCl -ethanol solution as the precursor. A series of 4 simple and effective procedures, such as stirring, rinsing, drying, carbonizing, calcinations, etc, were em- ployed. XRD, FESEM, and HRTEM analysis were carried out to investigate the structures and compositions of original pollen grains and the final products calcinated at different temperatures(300℃, 400℃, and 500℃). A detailed explanation is given on the biotemplating synthesis of porous hierarchical SnO nanomaterials. 2 Keywords: Porous Hierarchy; Tin Oxide; Biomorphic Nanomaterials; Pollen Grains 生物形态多孔分级结构氧化锡纳米材料的制备研究 位 莉 ，苏慧兰 ，宋 钫 ，文元振 ，张 荻 1* 1 1* 1 2 1 上海交通大学金属基复合材料国家重点实验室，上海 2 韩国基础科学支援研究院光州分院，光州，韩国 Email: hlsu@; venus_wei@163.com 收稿日期：2011年 3月 30日；修回日期：2011年 4月 26日；录用日期：2011年 4月 29日 摘 要：利用生物模板（油菜花粉）自身的分级结构，以四氯化锡酒精溶液为前躯体，通过搅拌、清洗、 干燥、碳化、煅烧等简单有效的处理方法制得了与油菜花粉内部结构相似的三维有序多孔结构氧化锡纳 米材料。采用 XRD、FESEM、HRTEM测试手段，从结构、组织和成分方面，对天然生物材料和不同煅 烧温度下(300℃、400℃、500℃)所制备的氧化锡遗态材料进行了对比研究，并详细阐述了模板复制过程 及生物模板在遗态材料合成过程中的作用。 关键词：多孔分级结构；氧化锡；遗态材料；花粉 1. 引言 价值而引起广泛关注。目前制备多孔分级结构纳米材 料的方法有很多，如煅烧前驱体法、溶胶-凝胶法、热 多孔分级结构纳米材料除了具备纳米材料典型的 [6] 分解法等 。但由于工艺条件的限制，这