以高炉铁水和废钢为主原料的不锈钢冶炼工艺及实践.pdfVIP

第28卷　第 4 期 Vol 28 , No4 　 上 　海 　金 　属 27 2 0 0 6 年 7 月 SHANGHAI METALS July , 2 0 0 6 以高炉铁水和废钢为主原料的不锈钢冶炼工艺及实践 池和冰 　李冬刚 　江庆元 　茅卫东 (宝山钢铁股份有限公司不锈钢分公司 , 上海　200431) 　　【摘要】　分析和介绍了宝钢不锈钢分公司以高炉铁水和废钢为主原料的不锈钢冶炼工 艺和实践 , 生产实践表明 , 与全废钢为原料的冶炼工艺相比 , 具有明显的优点 , 是一种高效 经济的不锈钢冶炼工艺。 【关键词】　不锈钢冶炼 　主原料铁水 + 废钢 　二步法冶炼 　三步法冶炼 STAINLESS STEELMAKING BY USING BF HOT METAL AND SCRAP AS MAIN RAW MATERIALS Chi Hebing 　Li Donggang 　Jiang Qingyuan 　Mao Weidong ( Stainless Steel Branch , Baosteel) The refining technology of stainless steelmaking by using BF hot metal and scrap 　　【Abstract 】 　 as main raw materials and its practice in Stainless Steel Branch of Baosteel were analyzed and introduced. The industrial practice indicated that in comparison with the process using total scrap as raw material , it was of obvious advantages , and a high effective and economic way for stainless steelmaking. 【Key Words 】 　Stainless Steelmaking , Main Raw MaterialsHot Metal + Scrap , Duplex Refining , Triplex Refining 1 　前言 选择以高炉铁水和废钢为主原料的不锈钢冶 宝山钢铁股份有限公司不锈钢分公司引进了 炼工艺路线 , 主要是基于降低能耗和成本 , 减少 世界一流的不锈钢冶炼技术 , 于 2004 年 4 月建 废钢用量 , 简化原料管理等方面的考虑。 成一条以高炉铁水和废钢为主原料的不锈钢生产 以高炉铁水代替全部碳钢废钢, 其自身的物 线。该生产线投产后 , 当年即产出 20 万 t 不锈 理热可大幅降低电炉熔炼所需的电能。采用 50 钢 , 并在不到一年的时间里通过技术攻关和生产 %～70 % ( 文中均为质量百分比) 高炉铁水作 实践 , 于 2005 年 3 月实现了月达产目标。在快 为电炉主原料后 , 不仅消除了不锈钢废钢和优质 速达产的同时 , 宝山钢铁股份有限公司不锈钢分 碳钢废钢供应不足之虞 , 且