制钠电解槽流场的模拟研究-有色金属（冶炼部分）.doc

40 kA制钠电解槽流场的模拟研究 刘中兴，张惠，伍永福，王亮亮 （内蒙古科技大学 能源与环境学院，内蒙古包头 014010） 摘要：电解质在阳极气泡和阴极钠液浮力的作用下在制钠电解槽内循环流动，是典型的气液液三相流动。使用FLUENT软件建立40A制钠电解槽三维流场数学模型，通过计算得到了电解槽内气泡、钠液的浓度和速度分布情况，以及熔盐的流场分布图。 关键词：钠电解槽气泡多相流流场TF826+.2 文献标识码：A 文章编号：1007-7545（2012）09-0000-00 Numerical Simulation of Flow Field in 40 kA Sodium Electrolytic Cell LIU Zhong-xing, ZHANG Hui, WU Yong-fu, WANG Liang-liang (School of Environment and Energy, Inner Mongolia University of Science and Technology, Baotou 014010, Inner Mongolia, China) Abstract：lowing cyclically in sodium electrolytic cell due to the buoyant force impact of bubble on anode and sodium on cathode, the electrolyte was a typical air-liquid-liquid triphase flow. The three-dimensional flow field mathematic models of 40 kA sodium electrolytic cell were established with FLUENT software. The concentration and velocity distribution of bubble and sodium, as well as the flow field of molten salt, were obtained through calculation. Key words：sodium electrolytic cell; bubble; phase flow; flow field; numerical simulation 制钠电解槽中电解质的流动是阳极气泡及阴极钠液上浮运动造成的[1-2]，这种运动在促使电解质温度与成分更均匀分布的同时也降低了电流效率。因此，有必要对熔体流场进行研究[3-] 。 1 电解槽模型 以40 kA制钠电解槽为模拟的实际原型如图1所示。熔体在制钠电解槽内的流动属于气液液三相流动。阴极和阳极均为圆筒形轴对称结构四组电极均匀分布于方形电解槽内，为简化模型，选择电解槽的1/4进行模拟。 图1电解槽结构示意图 Fig.1 chematic diagram of electrolysis cell 2 数学模型的建立 基本假设和边界条件参考文献[5-6]。 2. 电解槽内气液液三相流数学模型 采用欧拉模型对电解槽内流场进行模拟计算。电解槽内的熔体可以看成不可压缩流体[7]，采用连续方程[10]、动量方程[]和双方程[1-14] 组成的方程组来求解流场。收稿日期：2012-04-基金项目：国家自然科学基金资助项目 作者简介：刘中兴（1963-），男，河北赵县人，教授. （1） （2） （3） （4） (5) (6) (7) (8) 3 模拟结果及分析 3.1电解槽内气泡对流场的影响图气泡流场浓度云图 图气泡流场浓度云图 Fig.ubble flow field (a) and concentration (b) 由图可看出，阳极气体主要在阴阳极之间的区域流动，气泡流速从阳极外表面到阴极内表面逐渐减小，从阳极末端到靠近熔体上表面不断增，最大值阳极上部靠近熔体上表面处。由图可以看出，阳极气泡主要分布在阳极表面和上部熔体中。电解于稳定，在阳极