学兔兔 · 材料·工艺·设备· 激光淬火工艺在覆盖件拉延模具中的应用 荆、亚伟 (陕西重型汽车有限公司 车身分厂) 摘 要：在汽车覆盖件冲压成形过程中，拉毛缺陷十分普遍。对于产品而言，制造工艺对覆盖件表面质量的要求 十分严格，因为任何微小的拉毛缺陷都会在涂漆后影响漆层的美观，并降低其抗腐蚀性、缩短使用寿命。激光表 面淬火强化工艺是目前应运比较广泛的一种模具表面强化工艺，能够有效的提高模具表面硬度、耐磨性、抗粘 结性，改善制件拉毛缺陷。本文主要探讨汽车覆盖件产生拉毛现象的机理和改善措施。 关键词： 拉毛缺陷 激光淬火 耐磨性 抗粘结性 Application of Laser surface hardening process in stamping die Abstract：In the automotive coveting workpiece stamping process，scuffing defects are very CO1TI1TIOn．For the products， the manufacturing process of covefing workpiece quality requirements is very stringent，since any small scuffing would affect the paint in the painting of the beautiful，And to reduce its resistance to corrosion and reduction of service life．Laser surface hardening process is applied to strengthen the die surface process that can effectively improve the die surface hardness，wear resistance，anti-caking and improve the workpiece scuffing defects．This article explores the phenomenon of automotive coveting workpiece scuffing defects mechanism and improvement measures． Keywords：scuffing defects Laser hardening wear resistance Anti—caking 在汽车覆盖件冲压成形过程中，拉毛缺陷十分 首先是表面上那些凸起的顶点，由于承压面积小， 普遍，而制造工艺对覆盖件表面质量的要求十分严 这些凸部接触部分的单位面积压力非常之高，刚开 格，因为任何微小的拉毛缺陷都会在涂漆后影响漆 始是表面的高点油膜先失去，吸附层破坏，产生原 层的美观，并降低其抗腐蚀性、缩短使用寿命。在 子级接触而出现冷焊现象。模具表面和板料表面的 我公司主打车型德龙F2000驾驶室覆盖件中，采用 金属离子相互吸附、扩散，由于板料轧制和模具铸 目前比较先进的整体式一次拉延成型冲压工艺，消 造或加工等产生晶粒缺陷，两种洁净表面金属离子 除了过去多个冲压件点焊连接产生的累积误差，而 吸附力大于有缺陷的原子键或正常原子键，板料晶 且提高了生产效率，降低了整车生产成本。由于汽 粒被剥离、粘结在模具表面上，随着拉延继续深入， 车覆盖件由小变大，由简单浅拉延变为复杂曲面深 板料连续滑过模具表面，这些先粘附高点更易挤压 拉延，这对于冲压工艺的设计和模具制造水平提出 破坏板料表面油膜而吸附、扩散和剥离板料表面， 了更高的要求。生产过程中，