大掺量钢矿渣复合粉混凝土基本性能试验研究.pdfVIP

学兔兔 2015年第2期 混凝土与水泥制 品 2015 No．2 2月 CHINA CONCRETE AND CEMENT PR0DUCTS February 大掺量钢矿渣复合粉混凝土基本性能试验研究 李 阳 (上海市建筑科学研究院，200032) 摘 要：对普通混凝土、大掺量矿渣粉混凝土和大掺量铜矿渣复合粉混凝土分别进行了基本性能试验研究，包 括塑性混凝土性能、硬化混凝土力学性能和耐久性。试验结果表明，大掺量铜矿渣复合粉混凝土具有早期强度高、塑 性收缩和干缩低、耐久性好等特点。 关键词：普通混凝土；大掺量矿渣粉混凝土；大掺量铜矿渣复合粉混凝土；力学性能；耐久性 Abstract：The basic properties of ordinary concrete，concrete mixed with a large amount of slag power and concrete mixed with a large amount of steel slag composite powder are studied including the plastic properties of concrete，the me— chanical properties and durability of hardened concrete．The test results show that the concrete mixed with a large amount of steel slag composite powder has good technical characteristics，such as high early strength，low plastic shrinkage and dry shrinkage，good durability． Key words：Ordinary concrete；Concrete mixed with a large amount of slag power；Concrete mixed with a 1arge amount of steel slag composite powder；Technical characteristics；Durability 中图分类号：TU528 文献标识码：A 文章编号：1000—4637(2015)02—89—04 0 前言 率仅为55％，特别是钢渣的利用途径较少，主要用 近年来。随着GB／T 18046—2008(用于水泥和混 于工程回填和筑路，附加值较低。国家鼓励“推广生 凝土中的粒化高炉矿渣粉》标准的出台，以及国内 产钢铁渣复合粉作水泥和混凝土掺合料”{11。因此， 钢铁厂矿渣粉生产线的陆续投产，矿渣粉和粉煤灰 应加快研发钢渣矿渣双掺和大掺量应用技术。 双掺技术已经普遍被预拌混凝土企业所采用，但矿 本文以超细钢渣粉和脱硫石膏作为辅助胶凝 渣粉和粉煤灰的掺量一般较低，分别占胶凝材料总 材料和激发材料，与矿渣粉复配开发出一种新型钢 量的15％～18％左右，如果进一步提高掺量，将明显 矿渣复合粉。与普通混凝土相比，大掺量钢矿渣复 降低}昆凝土的早期强度，影响施工进度，尤其在冬 合粉混凝土用于一般工业与民用建筑在技术经济 季施工。大掺量矿渣粉混凝土尽管已在东海大桥、 上具有相当的优势。 杭州湾跨海大桥等重大工程中应用，但主要用于生 1 试验原材料 产蒸养预制构件，在一般工业和民用建筑中仍应用 1．1 主要原材料的化学成分 较少。