2014届本科毕业论文 化工设备的腐蚀与防腐研究 化工设备腐蚀与防腐研究 摘要 化工设备的腐蚀从现象上有全面腐蚀，局部腐蚀，从腐蚀机理上有化学腐蚀，电化学腐蚀。其中电化学腐蚀是最普遍，危害也最大的一种腐蚀形式。通过合理选材，优化设备，电化学保护，耐腐蚀涂料可以减缓和防止化工设备的腐蚀。所有化工设备产生腐蚀的原因，75%都是因为表面处理不当引起的。目前用耐腐蚀涂料来防止化工设备表面腐蚀最为简单、经济、有效，具有良好的应用前景。 关键词：化工设备，腐蚀，防腐  Study on corrosion and anticorrosion chemical equipment Abstract The corrosion of chemical equipment from corrosion, a comprehensive corrosion, localized corrosion. From a chemical corrosion mechanism of corrosion, electrochemical corrosion. The electrochemical corrosion is the most widespread, a form of corrosion damage is the largest. Through the rational optimization of material, equipment, electrochemical protection, corrosion resistant coatings can slow and prevent the corrosion of chemical equipment. The corrosion causes of all chemical equipment, 75% is because the surface is caused by improper handling. The corrosion resistant coating to prevent corrosion of chemical equipment is simple, economic, effective, and has a good prospect of application. Key words：Chemical equipment，Corrosion，Anticorrosive 目录 1引言1 2常见的腐蚀种类2 2.1全面腐蚀2 2.2 局部腐蚀3 2.2.1电偶腐蚀3 2.2.2 小孔腐蚀3 2.2.3 缝隙腐蚀3 2.2.4 晶间腐蚀3 2.2.5 选择性腐蚀3 2.2.6 磨损腐蚀4 2.2.7 应力腐蚀4 2.2.8 腐蚀疲劳4 2.2.9 氢损伤4 2.3 化学腐蚀4 2.4 电化学腐蚀4 3 化工设备防腐的措施5 3.1合理选材，优化设备6 3.2 电化学保护6 3.3 表面涂层防腐6 3.3.1耐腐蚀涂料7 3.3.2 其他表面工程技术7 4工程应用实例7 5结语8 参考文献9 致谢11   PAGE \* MERGEFORMAT 11 1引言 改革开放至今, 随着人民生活水平的提高，社会生产力的发展，我国经济有了很大的发展,工业化的进程也大大加快,化工设备使用范围也变得广泛,这对于化工设备的性能都有很高的要求,化工设备的正常运行直接关系着工程的正常生产和运作。腐蚀，是影响化工设备的主要问题，使化工企业的生产成本提高，影响化工企业效益,由腐蚀所带来的损失也越来越严重[1]。 全世界每90秒就有一吨铁变成铁锈，然而炼制一吨铁所需的能源可供一个家庭三个月之用。1999年统计，我国因腐蚀造成的损失约2800亿元，占国民经济总产值的5%左右[2]。 1975年芝加哥一大的炼油厂一根15cm的不锈钢弯管破裂引起爆炸，停产6周，这次腐蚀事故总维修费50万美元，停产造成的税收损失高达500万美元[3]。 腐蚀不仅影响设备的使用寿命，而且使得设备的检修周期缩短，增加非生产时间和修理费用；腐蚀使设备及管道的跑、滴、漏现象更为严重，使原料和成品造成大量的损失，影响产品的质量，污染环境，危害人的身体健康[4]，腐蚀引起的设备爆炸、火灾事故，使设备遭到破坏而停止生产，造成巨大的经济损失甚至危及人的生命。因此研究腐蚀对化工设备的影响极其重要。 化工设备是指化学工业生产中所用的机器和设备的总称。在现代生产环境下，化工设备都十分巨大，采购费用也都相当惊人，十万，百万，甚至上千万，但是在化工企业生产环境下，化工设备的腐蚀都是相当严重的