EDM电极快速精铸有限元模拟研究.pdfVIP

学兔兔 Ju1．2010 VO1．59 NO．7 ·685· EDM电极快速精铸有限元模拟研究 张 芳 (淄博职业学院机电工程系，山东淄博255314) 摘要：研究了EDM电极快速精铸凝固过程中铸型和铸件间的相互作用。利用接触单元法对铸型／铸件的边界进行处理， 以及对半圆柱铸件在凝固中尺寸变化进行了模拟。从而为实际工艺过程补偿量大小的确定提供理论依据和指导。 关键词：电火花加工电极；有限元模拟；快速成形 中图分类号：0242．21 文献标识码：A 文章编号：1001—4977(2010)07—0685—04 Finite Element Simulation of Rapid Precision Casting on EDM Electrodes ZHANG Fang (Mechanical and Electronic Engineering Department，Zibo Vocational Institute， Zibo 255314，Shandong，China) Abstract： The interaction between the mold and casting was studied in the process of rapid precision casting solidification of EDM electrodes．By using of the contacting element method， boundary of mold and casting was disposed and the dimension changes of semi-cylindrical casting were simulated in the process of solidification．The results provide theory basis and guidance for determining the compensation rate in actual process． Key words：EDM electrodes；finite element simulation；rapid prototyping R~／RP技术与精密铸造相结合进行快速模具制造 和铸型接触时，二者之间会存在机械作用。铸件与铸 是一种先进的制造技术，其铸型是具有一定厚度的复 型的接触和摩擦是铸件凝固过程热力耦合分析中许多 合陶瓷型壳，在高温下浇注得到精密复杂的铸件。实 临界应力的来源，并且铸型的材质也直接影响着凝固 际生产中是靠经验值来对铸件预先进行尺寸补偿 (一 过程中铸件尺寸精度的分析。③铸件凝固过程中，由 般补偿量为1％～3％)，但不同条件和环境下得到的经 于温度变化引起的铸型膨胀或收缩将直接影响铸件尺 验值也不一致，有时还不准确。 寸精度的分析。 1．3 潜热问题的处理 1 EDM电极凝固过程的有限元模拟 ANSYS中通过定义材料随温度变化的焓值考虑潜 与普通的砂型铸造相比，快速精密铸造具有两个 热【1l。焓值的变化量M-／可描述为密度、比热容及温度 特点：①铸型多为陶瓷型薄壳，蓄热能力有限；②在