增碳剂硫含量检测方法的对比分析.pdfVIP

学兔兔 增碳剂硫含量检测方法的对比分析 张婷婷 (上海市机械制造工艺研究所有限公司，上海201901) 摘要：介绍了增碳剂硫含量检测的标准方法，简述了艾氏卡法、高温燃烧法和库仑法的测试原 理和优缺点，用不同方法测试并对比了石墨、无烟煤和焦炭标样的硫含量。验证结果表明，艾 氏卡法准确度高、重复性好，而高温燃烧法和库仑法操作便捷，适用于日常大批量增碳剂硫含 量的分析。 关键词：增碳剂；硫含量；检测方法 中图分类号：TG223 文献标识码：A 文章编号：1673-3320(2015)01-0020-03 Comparison and Analysis of Test Methods for Sulfur Content of Carburetant ZHANG Tingting (Shanghai Machine Building Technology Institute Co．，Ltd．，Shanghai 201901，China) Abstract：The standard test methods for sulfur content of carburetant were introduced．and the testing principle of Eschka method，high temperature combustion method and Kulun method and their advantages and disadvantages were described briefly．The standard samples，such as graphite，anthracite COal and coke were tested and compared bv di毹rent methods．The results show that the Eschka method has high accuracy and good repeatability，and the high temperature combustion method and Kulun method with convenient operation are suitable for sulfur content of mass carburetant in daily testing． Key words：carburetant；sulfur content：test method． 增碳剂品种诸多，有木质碳类、煤质碳类、 碳剂的重要品质指标之一，准确而稳定地检测增 焦炭类和石墨类等。增碳剂中的硫元素能够大部 碳剂中硫含量是十分重要的。 分溶解在金属液中。对于炼焦用煤，其全硫含量 1 增碳剂硫含量的检测标准 高，煤中大约80％的全硫会转入焦炭中，造成炼 钢铁过程中大量的硫进入金属液中，使冶炼出的 测定增碳剂中硫含量国家标准的相关内容如 钢铁变脆…。此外，增碳剂中带入少量的硫，对 表1所示。针对不同种类的增碳剂，可采用相应的 高强度铸铁性能影响较大【2】。因此，硫含量是增 技术标准进行测定。 表1 增碳剂硫含量的检测标准 收稿日期：2014-09-02 作者简介：张婷婷 (1987一)，女，助理工程师，主要从事铸造材料的分析研究 20 l 2。l5年第l期 学兔兔 学兔兔 在硫标样质量和含硫量一定的情