大截面高铬铸铁铸件材质的选用.pdfVIP

维普资讯 学兔兔 Mar．2008 VOI．57 NO．3 大截面高铬铸铁铸件材质的选用 周 寒，杨震华，陈淑萍，贺 杨 (北方重工沈阳重型集团股份有限责任公司铸钢产业公司，辽宁沈阳110025) 摘要：对普通高铬铸铁、加B高铬铸铁、加Ti高铬铸铁和加RE高铬铸铁进行了铸态组织比较，并进行了热处理组织和性 能，及淬透性和耐磨性能试验分析。结果表明：加B高铬铸铁组织稳定，具有较好的淬透性和淬硬性，截面硬度均匀一 致。加B高铬铸铁可以满足水泥立磨磨辊上截面铸件 (≥200mm)的生产需要。 关键词：含B高铬铸铁；变质处理；耐磨性 中图分类号：TG143．5 文献标识码：B 文章编号：1001—4977(2008)03—0298—03 Selection of Materials for High ChrOmIum Cast Iron Castings with Th ick Cross Section ZHOU han，YANG Zhen—hua，CHEN Shu—ping，HE Yang (Cast Steels Industry Company，NHI Shenyang Heavy Machinery Group，Co．Ltd．，Shenyang 1 1 0025，Liaoning，China) Abstract： Comparisons of the as—cast microstructures were conducted between common high chr0mium cast iron and high chromium cast iron containing B and Ti as well as R E．respectively．to determine material suitable for thick cross—sectional castings，and their heat treated micr0structures， properties，hardenability and wear resistance were also analyzed through test．The results showed that the high chromium cast iron containing B has stable micr0structure and better hardenability．and the hardness along the cross section distributes homogeneously．Therefore the high chromium cast iron with B can meet the requirement of castings for vertical cement mill roller tire．whose cross section above 200 mm． Key words：high chr0mium cast iron containing B：modification；wear resistance 随着我国经济飞速发展，新建电厂装备磨机越来越 分别加入Ti、B、RE而得，4炉成分设计如下。 多，耐磨件需求量相应增加。特别是一些大型水泥磨项