孕育剂加入量对灰铸铁试棒抗拉强度的影响.pdfVIP

学兔兔 Aug．2010 铸 造 VO1．59 N0．8 FOUNDRY 孕育剂加入量对灰铸铁试棒抗拉强度的影响 李训华。，孔英杰 ，路 路 ，白广跃 (1．北京福田环保动力股份有限公司沈阳铸造厂，辽宁沈阳110117；2．沈阳鸿本机械有限公司，辽宁沈阳I10027) 摘要：从炉前孕育剂加入量对三角试片白口宽度、终硅量的影响，探究孕育剂加入量对试棒抗拉强度的影响，进而确 定正确的炉前孕育剂加入量，稳定铸件的力学性能。 关键词：孕育；白口宽度；终硅量；试棒抗拉强度 中图分类号：TG253 文献标识码：A 文章编号：1001—4977(2010)08—0841—03 Effect of I noculant Addition on Tensile Strength of Grey Iron Test Bars LI Xun—hua’，KONG Ying-jie’，LU Lu’，BAI Guang-yue (1．Shenyang Foundry Plant，Beijing Foton Environmental Engine C0．，Ltd．，Shenyang 1 101 17， Liaoning，China；2．Shenyang Honbase Machinery Co．，Ltd．，Shenyang 1 10027，Liaoning，China) Abstract：The effects of inoculant addition amount on white width and the finaI content of silicon in the triangular test piece were investigated，by which to study the influence of inocula nt addition on the tensile strength of test bars．The correct addition of the inoculant was determined，and stable the mechanical properties of engine castings were obtained finally． Key words：inoculation；chill width；final silicon content；tensile strength of test bar 我厂主要生产缸体、缸盖类铸件，材质牌号为 2 孕育剂加入量对试棒抗拉强度的影响 HT250，化学成分选择高碳当量 (3．9％--4．1％)，低合金 化 (0-3％～0．6％Cu、0．1 5％～0．40％Cr、0．03％～0．07％Sn) 2．1 试验方法 的处理方式，炉前采用0．2％SiBa+(0．1％~o．3％)SiFe孕 在生产现场，采用冲天炉一中频感应电炉双联熔 育剂进行孕育处理，金相组织要求：石墨形态为A型， 炼工艺，炉前处理采用专用孕育剂添加漏斗，随流孕 珠光体含量不低于98％，试棒抗拉强度要求达到 育处理，孕育时间占出铁时间的70％，800 kg浇包浇 230～280 N／mm 。 注，试验用 30 n3in圆棒做抗拉试棒。 2008年以前，生产的缸体、缸盖类铸件的具有 孕育处理前原铁液的C、Si含量，采用天津撒布朗 相同化学成分的试棒的抗拉强度波动较大，一般为 斯NSP550热分析仪检测，孕育处理后的铁液，采用瑞 30～50 N／mm ，为了探讨其波动的原因，从炉前孕育剂 士ARI公司的真空直读光谱仪进行检测，抗拉试棒的化 加入量对三角试样白口宽度、终硅量的影响，探究孕