Cortisomol根管糊剂根尖封闭能力的实验研究 　　作者：肖丹　高燕　黄小兰 　　［摘要］ 目的：探讨Cortisomol根管封闭剂的根尖封闭能力。方法：选取44颗离体单根管恒牙，随机分为2组，每组20颗牙，分别用Cortisomol糊剂和氧化锌丁香油糊剂加牙胶尖以冷侧压法充填根管，采用染料渗入法测量染料渗入距离。结果：Cortisomol糊剂组与氧化锌丁香油糊剂组根尖微渗漏均值分别为（1.21±0.47） mm和（2.17±1.08） mm，经t检验，P0.01，两组渗漏值具有显著性差异。结论：Cortisomol根管糊剂对根尖的封闭能力优于传统的氧化锌丁香油糊剂。 　　［关键词］ 根尖封闭 Cortisomol糊剂 染料渗入法 微渗漏 　　An Experiment Study on Apical Sealing Ability of Cotisomol Paste. 　　XIAO Dan, GAO Yan, HUANG Xiao-lan. 　　The Oral Hospital of Zhu Hai, Zhuhai 519015 　　［Abstract］Objective: To investigate the apical sealing ability of the Cotisomol paste. Methods: Fourty-two extracted single-rooted human teeth were randomly divided into two equal groups, each with 20 teeth. They were then respectively filled with Cotisomol paste or zinc oxide eugenol paste plus gutta-percha point. Apical microleakage was measured by dye penetration. Results: The apex of microeffusion was 0.93±0.42 mm in Cotisomol group and 2.89±1.082mm in zinc oxide eugenol paste group, showing significant difference in the t test, (P0.01). Conclusions: Cotisomol paste has better root canal seal ability than zinc oxide eugenol paste. 　　［Key words］ Apical seal Cotisomol paste Dye penetration Microleakage 根管充填是根管治疗中最重要的一步，其目的是封闭根管系统，尤其是根尖1/3，以防止细菌进入造成根管的再感染。而糊剂的使用是根尖封闭质量的关键［1］。据统计，根管治疗失败有近60%是由于根管封闭不完全造成的［2］。因而研究者一直都在寻找理想的根管充填材料和方法以彻底封闭根管系统。Cortisomol是目前国外常用的一种根管充填材料，现在国内也开始使用，关于其减轻根尖术后的疼痛及对治疗牙髓和根尖周病有较好的疗效［3］已有报导，而其对根尖孔的封闭能力报导较少。本实验通过染料渗入法将Cortisomol糊剂与传统的氧化锌丁香油糊剂对根尖孔的封闭性能作对比研究。 　　1 材料与方法 　　1.1 材料 Cortisomol根管糊剂（法国碧蓝公司生产），粉由1.1%醋酸强的松龙盐、多聚甲醛、氧化锌、红色氧化剂及赋形剂等组成，液为丁香油，应用方法为粉液调拌；氧化锌丁香油糊剂（上海齿科材料厂生产），其主要成份为氧化锌和丁香油，使用时两者调拌而成；牙胶尖（广东协禾医药有限公司生产）。 　　1.2 方法 　　1.2.1 样本收集和分组 收集离体单根管恒牙44颗，要求牙体完整，牙根长度近似。超声波去除牙面肉芽和结石，10%福尔马林液浸。 　　1.2.2 根管预备和充填 将以上所有牙均用金钢砂片于釉牙骨质交界处切除牙冠，拔除根髓后测量并记录根管工作长度（根管口至根尖孔上方1旁mm处的距离），用Ｋ型根管锉按常规法清理并扩大根管至40#，3%过氧化氢液和生理盐水交替反复冲洗根管后吸干。采用冷侧压法按测量好的工作长度进行根充，阴性和阳性对照组根管仅充填牙胶尖；A、B组各20颗分别用Cortisomol糊剂和氧化锌丁香油糊剂加牙胶尖充填根管，拍X片证实充填良好后，将以上各