固体多相催化剂的制备、表征和性能研究.pdfVIP

物理化学基础实验（下） 固体多相催化剂的制备、表征和性能研究 PBXXXXXXXX XXX 固体多相催化剂的制备、表征和性能研究 XXX PBXXXXXXXX XXXXXX@mail.ustc.edu.cn 中国科学技术大学，化学与材料科学学院，化学物理系 合肥，安徽 230026，中华人民共和国 摘要： 本实验采用浸渍法制备铈-锰复合催化剂，对催化剂进行差热 分析，测定了催化剂的比表面积，并进行了催化剂催化乙烯分解的反 应研究.通过对实验结果的分析，比较研究不同催化剂配比对催化剂 活性的影响. 关键词：物理化学 催化剂 差热分析 比表面积 活性 Research of Preparation, Characterization and Properties of Solid Heterogeneous Catalysts XXX PBXXXXXXXX XXXXXX@mail.ustc.edu.cn Departments of Chemistry and Material Science, University of Science and Technology of China Hefei, Anhui 230026, P.R.China Abstract: In this experiment, the Ce-Mn solid catalyst was prepared by the impregnation method. The catalyst was subjected to differential thermal analysis, and the specific surface area of the catalyst was determined by the BET method. Then we conducted a study on the catalytic decomposition of ethylene. Through analyzing the experimental results, the effect of different catalyst ratio on the activity of the catalyst was compared. Keyword ：Physical Chemistry, Catalyst, Differential thermal analysis, Specific surface area, Activity 1 / 19 物理化学基础实验（下） 固体多相催化剂的制备、表征和性能研究 PBXXXXXXXX XXX 1. 前言 1.1. 浸渍法制备固体多相催化剂 许多热力学上容易发生的反应在动力学上是不容易实现的，这是 因为反应路径需要比较大的活化能，从而使反应速率相当小.使用催 化剂往往能改变反应路径，大大减小速控步骤的活化能或总包反应的 表观活化能，这使得总反应速率有非常明显的提高，从而让一个热力 学上可以发生的反应在动力学上也可以实现. 本实验采用浸渍法制备铈-锰复合催化剂.当多孔载体与溶液接触 时，由于表面张力作用而产生的毛细管压力，使溶液进入毛细管内部， 然后溶液中的活性组分再在细孔内表面吸附.浸渍溶液中所含的活性 组分，应具有溶解度大、结构稳定和受热分解为稳定化合物的特点， 如硝酸盐、乙胺盐、胺盐等. 本次实验中使用的催化剂以锰为主，铈为辅，并且以活性氧化铝 颗粒为载体，主要用于催化小分子有机物的分解反应. 1.2. 差热分析法 物质在加热或冷却过程中常有物理或化学变化发生，同时有热效 应伴随产生，差热分析（DTA ）就是研