35、无粘结预应力筋工工艺标准(435-1996)(国外英文资料).docVIP

35、无粘结预应力筋工工艺标准(435-1996)(国外英文资料) Non-bonded prestressing technical standards (435-1996) 1, scope, This process is suitable for the non-bonded prestressed concrete structures of the post-earthquake zone in Beijing. 2, construction preparation, 2 materials and main machine tools The steel wire and steel wire of the non-binding wire shall conform to the national standard prestressed concrete wire (GB5223) An 85), prestressed concrete steel wire (GB5224? 5). 2.1.2 coating layer of unbonded tendons use special building oil, its performance, product quality indicators should comply with the bureau of hunan province issued on June 6, 1983, July 1, 1983 on a trial basis with unbonded prestressed antirust grease lubrication technical conditions requirement. 2.1.3 unbonded tendons wrapped layer material adopt high pressure low density polyethylene (the temperature at 190 ℃, the melt index was 1.5 ~ 5). 2.1.4 has produced the unbonded tendons of finished product quality requirements should comply with the standards in the Beijing area of the unbonded prestressed concrete structure (BUPC) rules for design and construction (try out) (DBJ01-7-90), the second part of chapter 2 article 2.2.5 requirements (see table 4-44). No adhesion steel wire, steel wire, no dead bending, see dead bend must be cut off. The wire should be long, and there is no joint. No bonded steel, coating, coating quality requirements and test method table 4-44 The top vertex allows the deviation (mm) check method The coating (building grease) is full of the appearance of each meter.Figure 4-54 b tensioned anchorage system side (1 a) 椉 throughout ? 椕  determined? 棾 wake arch already? 椔 Dang  farce? 椢 Jiao opportunist Chen? The performance and conditions of a/b anchor are shown in table 4-45. Usually wire bundles are made of a or b, and the steel strand is used in type b. The technical performance of the 2.1.6 supporting tensioning equipment with oil pump and jacks is shown in table 4-46. The machine has a c