粉煤灰中多种氧化物提取利用初探 　　摘要： 为了探索粉煤灰高附加值利用途径，利用微波辐射和机械粉磨的方式激化粉煤灰的活性，再利用微波加热和碱溶的方式提取SiO2和Al2O3等有价值的氧化物。实验结果表明：利用微波辐射和机械粉磨的方式可以激发粉煤灰的活性，在微波辐射30min、机械粉磨至320目占比80%左右、NaOH浓度2.5mol/L、液固比为40、反应时间30分钟后，SiO2提取率可达38%；同等条件下，控制钙硅比在2.2左右时，Al2O3的提取率可达90% Abstract： In order to explore the high added value utilization of fly ash， the activity of fly ash was intensified by microwave radiation and mechanical milling， and then the oxides of SiO2 and Al2O3 were extracted by microwave heating and alkali solution. Experimental results show that using microwave radiation and mechanical grinding can stimulate the activity of fly ash， in the microwave radiation for 30 min， mechanical grinding to 320 mesh accounted for more than about 80%， 2.5mol/l NaOH concentration， liquid to solid ratio 40， the reaction time 30 minutes later， SiO2 extraction rate could reach 38%； under the same conditions， control of calcium and silicon ratio at about 2.2， Al2O3 extraction rate can reach 90%. 关键词： 微波辐射；机械粉磨；粉煤灰；碱溶；三氧化二铝；二氧化硅 Key words： microwave radiation；mechanical grinding；fly ash；alkali solution；Al2O3；SiO2 中图分类号：TQ533 文献标识码：A 文章编号：1006-4311（2016）19-0110-03 0 引言 粉煤灰是燃煤电厂的副产品，产生量巨大。2014年底，国务院颁布的《能源发展战略行动计划2014-2020》指出，我国优化能源结构的路径是：降低煤炭消费比重，提高天然气消费比重，大力发展风电、太阳能、地热能等可再生能源，安全发展核电。到2020年，非化石能源占一次能源消费比重达到15%；天然气比重达到10%以上；煤炭消费比重控制在62%以内；石油比重为剩下的13%[1]。煤炭的消费比重虽然在下降，但仍未动摇煤炭作为主要燃料的地位。因而，粉煤灰的产生量在短期内并不会下降，大量排放的粉煤灰亟待合理处置。近年来，粉煤灰的综合利用已经成为行业共识，各国都在探索新的粉煤灰利用途径，拓展粉煤灰利用空间，从而实现这一工业废渣的无害化、减量化和资源化[2]。粉煤灰的主要化学成分是SiO2、Al2O3，这两种主要成分含量越高，粉煤灰的活性就越高[3] 目前，国内氧化铝的需求量不断增长，与此同时优质的铝土矿却面临枯竭，从粉煤灰中提取氧化铝就变得很有价值[4]。除此之外，由于粉煤灰颗粒较细、硬度较低等特点，可以免去复杂的矿石破碎和筛选的工序，使其具备替代铝土矿的优势。结合粉煤灰的物理化学特性来提取氧化铝，可以提供粉煤灰的综合利用水平，拓宽粉煤灰的高附加值综合利用途径，从而增大粉煤灰的消耗量。在提取氧化铝的同时，合理设计提取路线，可以把粉煤灰中的非晶态二氧化硅一并提取，用以生产白炭黑等硅质产品，可进一步提高粉煤灰综合利用的附加值，从而激活粉煤灰高附加值利用的市场活力。笔者及其团队利用微波加热和机械粉磨的方式激活粉煤灰的活性，在碱溶和微波加热条件下促进粉煤灰中有价值的Al2O3和SiO2溶出，从而探索一条腐蚀性弱、热能损失小、无二次污染的粉煤灰提取有价氧化物资源的新方法 1 原材料 实验用粉煤灰取自徐州市周边热电厂，分别对样品进行工业分析和元素分析，关注其中Al2O3和SiO2等活性成分。利用平均采样法采集徐州市周边热电厂的粉煤灰样品，分别利用氟硅酸钾容量法和EDTA直接滴定法对