等离子喷涂在密封隔环上的应用.pdfVIP

等离子喷涂在密封隔环上的应用 + + 中图分类号：TF123.1 44,TF125.3 1 文献标识码：B 文章编号：1004-4620(2000)03-0023-03 Application of Plasma Spraying Process in Sealing Caulking Ring 1 2 2 2 2 GONG Mao xiu ,NING Fu ju ,WANG Ming bo ,LIU Wen song ,XU Guang jie (1.Shandong Metallurgical Science Research Institute,Jinan 250014 China; 2.Laiwu Iron and Steel Group Co.,Ltd,Laiwu 271104,China) Abstract：Metallic oxide ceramic coat is coated on dynamic sealing caulking ring of roll bearing of 430 and 340 chuck mill,which is imported from foreign,used of plasma spraying process.Through reasonable selecting technical parameters and strengthening quality control,the sealing ring is successfully prepared.The production practice proves that the characters of this coat are high hardness,high resistance to wear,high resistance to corrosion,small frication factor,low energy consumption,etc. Keywords：plasma spraying;matallic ceramic coat;sealing caulking ring 1 前言 等离子喷涂是目前广泛使用的制备陶瓷涂层的高新技术。其原理是将气体(氢气、氮气,有时为了获得高温加入一定 的氩气或氦气)送入等离子喷涂枪内,通过高频点火电离成高温离子气体,经过阳极喷咀高速喷出,粉末用载气送入等离 子火焰中熔化和加速,喷涂到工件的表面。等离子喷涂可以产生极高的温度 (10000℃以上),因此特别适用于陶瓷涂层的 制备〔1～4〕。采用等离子喷涂技术在金属基体上制备陶瓷涂层,能把陶瓷材料的特点和金属材料的特点有机地结合起来,获 得复合材料结构及制品〔1,4,5〕, 用来最大限度地发挥金属和陶瓷各自的优点,拓展这些材料的使用范围。密封隔环是意大 利达涅利公司轧钢设备中430、340 卡盘轧机轧辊轴承动密封备件,笔者已在文献〔6〕中作了报导。采用等离子喷涂设 备及工艺技术,对其进行了金属陶瓷涂层的喷涂,选用氧化铬作为陶瓷涂层材料,取得了圆满成功。 2 陶瓷涂层喷涂设备及工艺 2.1 等离子喷涂设备〔7〕 由于等离子喷涂设备具有焰流温度高、速度快、气氛可控等一系列优点,因而非常适用于喷涂陶瓷材料。所用等离 子喷涂设备为美国产METCO 7M 型。该设备由等离子喷枪、喷涂电源、送粉器、气体供应系统、冷却水装置等部分组成。 2.2 陶瓷涂层的等离子喷涂工艺 2.2.1 基体表面预处理 为使涂层与基体有良好的结合强度,必须对受喷基体表面进行预处理:(1)净化处理：使基体 表面达到必要的清洁程度? (2)粗化处理：将净化后的基体表面形成凹凸不平的粗糙表面。只有经过粗化处理的基体才 能和涂层具有良好的结合力(本工作采用喷砂粗化处理)。 2.2.2 等离子喷涂工艺过程 等离子喷涂工艺过程中,影响涂层质量的因素很多,选择合理的工艺参数可以得到性能最 好的涂层。等离子喷涂工艺的主要工艺参数有:(1) 等离子射流参数：主要指焰流的温度、速度、热熔及气体成分。这 些参数又取决于等离子喷枪的结构、等离子气体种类、流量、电弧功率;(2)粉末参数: