TM HEV 用次世代高输出圆桶形镍氢电池 （PROTHIUM ） 的开发 Abstract The next-generation cylindrical nickel-metal hydride D-size battery PROTHIUMTM with remarkably high power and durability has been successfully developed for HEV applications. This was accomplished by main technologies: newly developed inner current collecting structure for drastic reduction of internal resistance to half value of existing one; positive active material coated by ytterbium contained composite oxides for high charging efficiency ; and alloy powder with high catalytic activity by special treatment, and alloy-corrosion-resistant additives for longer life. The specific power, power density, and cell power at 50% SOC were 1800 W/kg, 5750 W/l and 302 W/cell, respectively. Moreover, the cell has an additional feature capable of continuous discharge even at large current of 300 A at ambient temperature of 25 ℃． Key words : Cylindrical Ni-MH battery ; HEVs ; High power ; Long life 1， 前言 左右和更低，期望高输出化。 镍氢电池具有高能量密度，高输 出，且环境合适性和安全性的出众电 我们为了满足这些愿望，此次， 池，被混合电动汽车（HEV），电动汽 开发了同原来不同的溶接方法，实现 车（EV），电动工具广泛使用。特别 可能的集电构造。因此，成功地大幅 是HEV上搭载的电池，对马达驱动可 降低了电池的内部阻抗，实现了 实现必要的大电流放电，工作的环境 1800W/kg （5750W/l ）的高输出密度。 温度广泛，持有同汽车使用期限同等 而且，通过提高在正极的高温区的充 的以上的寿命耐久性，谋求高能量密 电 效 率 及 耐 久 性 ， 开 发 了 度，根据系统，至此包含圆桶形，方 （PROTHIUM ）TM 。以下，关于电 形等的电池形状，追求高性能化，小 池导入的新技术，新方法，对特性和 型紧密化。但是，现在实用化的 HEV 关联附加作了叙述。 用电池，在输出密度方面，方形是 1300W/kg 前后，圆桶形在 1000W/kg 2， 实验结果及考察 一般的圆桶形镍氢电池以卷转正 2．1 开发电池「PROTHIUM 」的规格 极板,隔板,及负极板极群,以及用电 表 1 显示密闭圆桶形 D 形镍氢电 连接正极集电极和盖,的导线板,电池