低品味海泡石在毛巾印花糊料中应用.docVIP

低品味海泡石在毛巾印花糊料中应用 　　摘要：海泡石是一种非金属粘土矿物，用途广泛，其所具有的流变性、悬浮性、增稠性和分散性等性能，为其在印花糊料中的应用提供了可能。本研究采用低品位海泡石与海藻酸钠进行复配来制备棉毛巾印花用新型糊料。研究结果表明，海泡石与海藻酸钠复配比例在3∶7、4∶6及5∶5时均可用于毛巾织物印花，其中4∶6时印花效果最佳。新型糊料安全环保，对环境及人体无毒无害，成本低，性能稳定 关键词：糊料；海泡石；印花；毛巾 中图分类号：TS194.2 文献标志码：A Application of Low Grade of Sepiolite in Paste for Towel Printing Abstract： Sepiolite is a kind of non-metallic clay mineral with a wide range of uses. The properties of rheology， suspension， thickening and dispersing of sepiolite make it possible to be applied in printing paste. A new printing paste was prepared with low grade sepiolite and sodium alginate through compounding. The application results showed that the new printing paste could be used in printing of towel fabric， when the compound proportion of sepiolite and sodium alginate was 3∶7， 4∶6 and 5∶5. Moreover， the printing effect would be optimal， when the proportion was 4∶6. The new paste is not only safe and environmentally friendly， non-toxic and harmless to the environment and the human body， but also stable and low-cost. Key words： paste； sepiolite； printing； towel 纯棉毛巾织物一般以 3 个系统纱线（毛经、地经和纬纱）相互交织，表面毛圈密集，织物风格相对粗犷、厚实，印花时对花型的精细度要求不高（丝网目数80 ～ 110目），但对其印透性要求较高。海藻酸钠糊是棉织物活性染料印花的首选糊料，具有色泽鲜艳、工艺简单、色牢度好等优点，但也存在黏度大，易出现沾网、拖带，存放过程中易结皮、变质及价格较高（4万 ～ 5 万元/t）等缺点 海泡石是一种层链状结构的含水富镁硅酸盐类非金属粘土矿物，具有安全环保等诸多优点，同时，其强大的功能使其高品位矿已在医药、环保、国防等领域广泛应用；而低品位海泡石受关注较少，但其所特有的流变性、悬浮性、增稠性和分散性等基本性能并未改变，再考虑到其明显的价格优势（低品位海泡石售价低于 1 万元/t），为其在纺织品印花糊料中的应用提供了可能 1 实验部分 1.1 材料、药品及仪器 1.1.1 实验材料 纯棉单面割绒漂白毛巾半制品（70 × 140 cm，克重300 g/m2，益阳龙源纺织有限公司） 海泡石粉末（纯度15%，细度300目，湘潭源远海泡石科技有限公司），颜色呈浅灰色，其基本化学组成如表 1 所示 1.1.2 实验药品 活性艳蓝KNR（无锡市丽马化工染料有限公司）；?碱、尿素、海藻酸钠、防染盐S（天津科密欧化学试剂有限公司） 1.1.3 仪器及设备 MU562A型印花实验机（北京纺织机械器材研究所），101-2型数显电热鼓风烘箱、LSD-400间歇式定形烘干小样机（佛山市南海区宏信机械设备有限公司），YG751B预制式染色摩擦牢度仪、SW-12D耐洗色牢度试验机（宁波纺织仪器厂），PR-HWS-28恒温水浴锅（上海瑞普赛斯仪器股份有限公司），XY系列精密电子天平（常州市幸运电子设备有限公司），NDJ-8S数字式黏度计（上海精天电子仪器有限公司），Datacolor 600电脑测色配色仪（Datacolor公司），JJ-1A型电动搅拌器（金坛市良友仪器有限公司），紫外-可见分光光度计（上海美谱达仪器有限公司） 1.2 糊料制备 1.2.1 糊料配方