TiO2光催化降解颜料生产废水的实验研究.doc

TiO2光催化降解颜料生产废水的实验研究 05化学教育1班 刘 磊 指导教师：雷新有 [摘 要] 本实验研究了催化剂、光源、溶液初始浓度、溶液初始pH值等因素对颜料生产废水光催化氧化降解反应的影响。实验结果表明，最佳实验条件为：以纳米 TiO2为催化剂，催化剂的投加量为1g·L-1，采用254nm紫外灯作光源，颜料生产废水初始浓度为100mg·L-1，溶液初始pH=3。该实验条件下，颜料生产废水一小时脱色率可达78.2%。[关键词] 颜料生产废水 光催化氧化降解 二氧化钛 Study on the Experiment of TiO2 Photocatalytic degradation in pigment wastewater LIU Lei (Department of Chemistry, Tianshui Normal University Gansu Tianshui 741001) Abstract: The experimental study of the catalyst,the light source,the initial solution concentration,solution pH value of the initial production of pigments and other factors on the photocatalytic oxidation of wastewater degradation reaction.The experimental results show that the best experimental conditions are as follows: for nano-TiO2 as a catalyst,catalyst dosage of 1g?L-1,using 254nm UV lamp for light source,the initial concentration of pigments for the production of wastewater 100mg?L-1,the early solution until pH=3.Under the experimental conditions,pigment production wastewater decolorization rate of up to 1 hours 78.2% Keywords: pigment wastewater photocatalytic oxidation degradation titanium dioxide 前言 随着颜料合成、印染等工业废水的不断排放及各种染颜料的不断使用，进入环境的颜料数量和种类在不断增加，我们的环境污染问题日趋严重。印染废水，特别 是含有偶氮、苯环、胺结构有机化合物的颜料废水，进入人体后对人体有致癌作用，并且印染废水具有水量大、水质变化大、有机污染物浓度高、可生化性差等特点，所以如何降解印染废水已成为一个亟待解决的问题。 半导体超细微粒如TiO2、CdSCO2、H2OTiO2因其光稳定性高、化学性质稳定、难溶、无毒、成本低、具有高效性等优点，已被广泛用于处理有机或无机废水。近年来，人们对以半导体为催化剂处理印染等含有机物废水的可行性进行了广泛的研究[1-5]。 半导体光催化反应体系中，影响生产废水光催化降解速率的因素有很多。本文研究了催化剂、光源、溶液初始浓度和溶液 pH 值等因素对光催化氧化降解颜料生产废水反应的影响，研究颜料生产废水在不同条件下的降解情况[6]。 1 实验部分 1.1 仪器与试剂 仪器：721型可见分光光度计（上海精密科学仪器有限公司），电子天平（梅特勒-托利多仪器（上海）有限公司），791 型磁力加热搅拌器（上海南汇电讯器材厂），高压汞灯（上海飞利浦照明有限公司），卤钨灯（30V 400W），254nm，365nm4B酸，2B酸及其相互反应的水溶性副产物。 准确量取颜料生产废水100 m1注入250m1烧杯中称其总质量，加热浓缩（100℃）称其剩余物和烧杯的质量，二者相减为废液里混合溶质的总质量，通过计算可知废液初始浓度为500 mg·L-1。 1.2.2脱色率的确定 反应器容积500m1，放置于磁力搅拌器，将已配制好的一定浓度的废液及一定量的TiO2粉末加入其中，搅拌，每隔半小时取样分析测其吸光度，光照一定时间后停止反应，同时做空白试验和暗反应对照试验，以消除非光解因素（如吸附）对降解的影响[6]。废液的脱色率用以下公式计算： 脱色率（%）= (A0-At)/A0×100% A0，