红色长余辉发光材料sr3al2o6eu2+,dy3+的合成与发光性能的研究本科论文.docVIP

红色长余辉发光材料Sr3Al2O6:Eu2+,Dy3+的合成与 发光性能的研究 摘 要 长余辉发光材料是一种关闭光源后仍能持续长时间发光的新型功能材料，被广泛应用于紧急照明、军事和工艺美术等领域。因为红色长余辉发光材料的欠缺在一定程度上抑制了长余辉发光材料的应用，所以新型红色长余辉发光材料成为了人们的研究热点，而Sr3Al2O6:Eu2+, Dy3+作为一种新型的红色长余辉发光材料，具备铝酸盐长余辉发光材料的优良特性，越来越受到人们的重视。 本文采用传统的高温固相法制备了Eu2+, Dy3+共激活的Sr3Al2O6红色长余辉发光材料。合成长余辉发光的最讨论了Sr/Al、Eu/Sr、Dy/EuB/Al以及煅烧温度对发光粉体的影响Sr3Al2O6:Eu2+, Dy3+发光粉体中掺杂第三种离子（S2-、Cr3+、Pr3+）的发光性能。 结果表明Sr3Al2O6:Eu2+, Dy3+发光粉体的激发光谱均为宽带谱，发射波长nm范围内变化，余辉时间最长达到。Sr/Al=2.00，Eu/Sr=0.04，Dy/Eu =1.50，B/Al=0.10；对余辉时间而言，合成发光粉体的最佳工艺为：Sr/Al=2.50，Eu/Sr=0.03，Dy/Eu=1.25，B/Al=0.15。 随着Sr/Al的增加，合成样品的主相由Sr3Al2O6变为Sr4Al2O7。Eu/Sr为5%时会引起浓度猝灭现象。适宜的烧结温度和B/Al会较好的形成Sr3Al2O6晶相。通过系统的比较，发现Sr/Al对Sr3Al2O6发光性能的影响最大，直接影响样品的发光颜色。 Sr3Al2O6:Eu2+, Dy3+, X3+（X=Cr，Pr）发光粉体的发射波长分别为696nm，624nm。S2-的引入生成了SrS相，改变了基质组成，从而使发射峰发生红移。 最后，应用Material Studio模拟了Sr3Al2O6的晶体结构，利用紫外-可见光谱计算了它的禁带宽度，通过对样品的热释光谱分析确定了Sr3Al2O6:Eu2+, Dy3+的陷阱能级深度，利用空穴转移理论构建了Sr3Al2O6:Eu2+, Dy3+的发光机理模型。 关键词：Sr3Al2O6长余辉发光红色RESEARCHES ON SYNTHESIS AND PHOTOLUMINESCENCE OF THE RED LONG PERSISTENT PHOSPHORS Sr3Al2O6:Eu2+,Dy3+ ABSTRACT The long photoluminescence phosphor is a new functional material which can illuminate for a long time after the lamp-house is closed. This material has been applied in lots of domains such as emergent illumination, military affairs, industrial arts and etc. Its application is restrained by the deficiency of the red long photoluminescence phosphor. Now the research on the new red long photoluminescence phosphors has been done and the Sr3Al2O6:Eu2+, Dy3+ phosphor has been thought much of because this phosphor posseses the excellent characteristics of the aluminates. In this paper, the red long persistent phosphors Sr3Al2O6:Eu2+,Dy3+ was successfully synthesized via conventional high temperature sintering method. The best synthetic condition was obtained by experiments. The effects of Sr/Al, Eu/Sir, Dy/Eu, B/Al and the sintering temperature on the phosphors were discussed. At last, the luminescence properties of Sr3Al2O6:Eu2+,Dy3+ phosphors adulterated by S