含锶磷酸钙骨水门汀的理化性能和水化产物论文.docVIP

　　含锶磷酸钙骨水门汀的理化性能和水化产物论文 .freelical properties and hydrating product of αtricalcium phosphate cement modified by strontium carbonate phosphate(αTCP) cement odified by strontium carbonate, the settingtime, pressive strength, rate of dissolution and value of pH and electron microscope. Results Strontium carbonate had no interference ent’s hydrating process. The settingtime could meet the expectation of clinical operation. The pressive strength and the rate of dissolution increased.The hydrating product hydroxyapatite containing ions.Conclusion Proper Strontium carbonate could improve the property of αtricalcium phosphate cement. The hydrating product ilar to nature bone and easy to connect phosphate; carbonic acid; strontium 磷酸钙骨水门汀(CPC)具有自固化性和良好的生物相容性,可作为抗生素、抗肿瘤药物和各种生长因子优良的缓释载体1。但CPC同时存在机械性能不足,降解缓慢等缺点,又使其应用受到一定程度的限制。对磷酸钙骨水门汀的改性研究已成为热门课题。羟基磷灰石中的钙能被锶置换生成锶磷灰石(SrHAP)。有研究表明SrHAP比HA具有更好的生物相容性和降解性能,为更好的骨缺损修复材料2。SrHAP在与骨结合界面处通过Ca、P、Sr等元素的溶解再沉积,与天然骨形成良好的结合3。SrHAP骨水门汀的植入试验观察到3个月时新骨形成,6个月时与周围骨组织形成紧密结合4。由于人体骨组织的无机成分中含有5%~8%的碳酸盐,根据仿生设计的原理,笔者选用碳酸锶对α磷酸钙骨水门汀系统进行改性研究,考察其理化性能及进行水化产物分析。 1 材料和方法 1.1 材料 1.1.1试剂与仪器 α磷酸三钙(αTCP)、磷酸二氢钙、羟基磷灰石、碳酸锶(四川大学生物材料教研室),电子式万能试验机(X1E),X射线光谱仪(XPert MPD,荷兰Philips公司),扫描电镜(JSE5900L,日本电子公司)。 1.1.2 固化体制备 α磷酸三钙、磷酸二氢钙、羟基磷灰石按一定物质的量的比例混合,分别加入物质的量的比例为5％,10％,15％,20％,25％或30％碳酸锶粉末,在研钵中研磨混合均匀,过400目筛,干燥备用。固化液为0.25 mol/L磷酸二氢钠/磷酸氢二钠缓冲溶液。CPC粉液按液固质量比(L/P)=0.35的比例均匀调和60 s,将浆体填充入6 mm×12 mm的圆柱形不锈钢模具,于37 ℃、100％湿度环境中固化,1 h后脱模,将固化体浸泡入PBS溶液中,37 ℃恒温水浴。以未加碳酸锶粉末的固化体为单纯组。 1.2 方法 1.2.1 测定凝固时间、压缩强度、溶解率和pH值 CPC粉液(L/P=0.35)均匀调和,将维氏针垂直放在骨水泥表面,停留5 s。每隔30 s重复1次,至维氏针针头在骨水泥表面未能留下圆形痕迹。从开始计时到试样表面无圆形痕迹的时间为凝固时间。重复5次,取平均值。 将脱模后的试样立即浸入37 ℃的PBS溶液中,恒温保持7 d。用电子式万能试验机(Pa。除15％组和单纯组压缩强度值差别有统计学意义外,其余各组和单纯组比较差别均无统计学意义。除5％组、10％组和单纯组的溶解率差别无统计学意义外,其余各组和单纯组比较差别均有统计学意义。表1 水门汀固化体性能测试值（略） 2.2 水门汀pH值 单纯组和含15％碳酸锶组水门汀的pH值在固化过程中逐渐降低,但单纯组pH值下降更剧烈。约2 h后二者均维持在一个比较稳定的水平(图1)。 2.3 X射线衍射分析 主要是HA、αTCP的特征衍射峰,同时存在着少量的其他杂质的谱线。HA的特征衍射峰具有较高强度而αTCP的特征衍射峰较弱(图2)。 2.4 红外线衍射光谱 1042 cm1的强而宽的峰是HA中PO3-4的伸缩