三聚氰胺甲醛硫脲螯合树脂的超声合成及应用研究.pdfVIP

2 三聚氰胺- 甲醛-硫脲螯合树脂的超声合成及应用研究 摘 要 采用超声法成功制备了三聚氰胺- 甲醛-硫脲螯合树脂。通过场发射扫 描电镜(FE-SEM)，透射电镜(TEM) 以及热重分析(TG)等对该螯合树脂的结 构和性能进行了表征。结果表明：该螯合树脂呈现均匀的球状，粒径在 200-500 纳米范围内；螯合树脂在升温至 80 之前质量基本维持恒定。℃ 合成的三聚氰胺- 甲醛-硫脲螯合树脂对银离子具有良好的吸附性能， 可用作制备纳米银催化剂的载体；在该螯合树脂上先行吸附诱体氯化钯溶 胶，以镀镍废液为原料，抗坏血酸为还原剂，原位制备了纳米镍/ 螯合树脂 复合材料。 关键词：三聚氰胺硫脲树脂；超声合成；纳米银；镀镍废液 I Ultrasonic Synthesis and Application of Melamine-Formaldehyde-Thiourea Chelating Resin ABSTRACT Melamine-formaldehyde-thiourea chelating resin was successfully prepared using ultrasonic method. The characteristics were investigated by field emission scanning electron microscope (FE-SEM), transmission electron microscopy (TEM), differential scanning calorimetry (DSC) and thermo-gra -vimetric analysis (TG). A great deal of well-proportioned spherical could be observed with a size of 200-500 nm. The resin would be depredated after temperature more than 80 ℃. The present melamine-formaldehyde-thiourea chelating resin showed a good adsorption for silver ion, which could be used as a carrier of nano silver. Furthermore, the inductor of PdCl 2 sol was adsorbed at the resin, then, nano -nickel could be reduced in suit by ascorbic acid in spent electroless nickel plating bath . Keywords : Melamine-thiourea resin; Ultrasonic synthesis; N ano-silver; Spent electroless nickel plating water II 致 谢 本论文是在导师晋冠平教授的悉心指导和严格要求下完成的。在研究 生阶段，晋老师渊博的学识、敏捷的科研思维、严谨的治学态度以及忘我 的工作精神，使我在工作中和生活中均深受教益。在此，向晋老师致以诚 挚的敬意和衷心的感谢。 感谢化学工程学院和校分析测试中心提供的优良实验条件，感谢老师 们在研究生阶段给予我的教育和指导。 感谢实验室的所有同学对我的支持和鼓励。 最后要特别感谢我的父母，他们毫无所求的支持和关怀是我取得的所 有成绩的基础，也将永远是我