冷冲模材料与热处理(国外英文资料).docVIP

冷冲模材料与热处理(国外英文资料) Cold stamping die, cold is used for material and heat treatment Die type Commonly used material Heat treatment Hardness (HRC) Die punch die The shape is simple, blanking the thickness of sheet material 3mm T8A, T10A, 9Mn2V, Cr6WV, GCr15, 45 # Hardening, tempering, 58-62 58-62 The shape is complex, blanking sheet material thickness 3mm, demand durable high CrWMn, 9 sicr, Cr12, Cr12MoV, Cr4W2MoV D2 Hardening, tempering, 58-62 58-62 Bending die General bending die T8A, T10A Hardening, tempering, 54 ~ 58 56 ~ 60 It is required to have high abrasion resistance, complex shape and large batch CrWMn, Cr12, Cr12MoV, Cr12Mo1V1 Hardening, tempering, 58-62 58-62 Thermal bending die 5 crnimo, 5 crmnmo H13, 3 cr2w8v Hardening, tempering, 48 ~ 52 48 ~ 52 Tensile modulus General tensile modulus T8A, T10A, GCr15 Hardening, tempering, 55 ~ 58 55 ~ 58 It is required to have high abrasion resistance and production batch large drawing die Cr12, Cr12MoV, YG8, YG15, D2 Cold working die Cold work mould fastener industry mainly complete metal or nonmetal material cutting, bending, drawing, upsetting and extrusion process, made into all kinds of bolts, screws, nuts, washers, pins, rivets, etc. Due to the different mechanical properties of loading and processing materials, the working conditions of various kinds of mould are very different and the failure forms are different. In the above mould, the die working condition is the worst of the working condition is the upsetting die, the squeeze mode, the second is the thick plate hole blanking the mold. The cold is the failure of the mould The upsetting die is mainly used for the manufacture of bolts, nuts and aliens. It is used for metal forming. The weight and weight of the mold are different depending on the shape, size, deformation and mechanical properties of the deformation materials. In production due to the deformation of metal in the turbulent flow in the mold cavity have serious friction, cause mould transient surf