* Figure The microstructure of BMT ceramics obtained by compaction and sintering of BMT powders. Figure Particles of barium magnesium tantalate (BMT) (Ba(Mg1/3 Ta2/3)O3) powder are shown. This ceramic material is useful in making electronic components known as dielectric resonators that are used for wireless communications. * Figure Grain growth occurs as atoms diffuse across the grain boundary from one grain to another * Figure Grain growth in alumina ceramics can be seen from the SEM micrographs of alumina ceramics. (a) The left micrograph shows the microstructure of an alumina ceramic sintered at 1350oC for 150 hours. (b) The right micrograph shows a sample sintered at 1350oC for 30 hours. * Figure The steps in diffusion bonding: (a) Initially the contact area is small; (b) application of pressure deforms the surface, increasing the bonded area; (c) grain boundary diffusion permits voids to shrink; and (d) final elimination of the voids requires volume diffusion 人有了知识，就会具备各种分析能力， 明辨是非的能力。 所以我们要勤恳读书，广泛阅读， 古人说“书中自有黄金屋。 ”通过阅读科技书籍，我们能丰富知识， 培养逻辑思维能力； 通过阅读文学作品，我们能提高文学鉴赏水平， 培养文学情趣； 通过阅读报刊，我们能增长见识，扩大自己的知识面。 有许多书籍还能培养我们的道德情操， 给我们巨大的精神力量， 鼓舞我们前进。 * * Section 4.2 扩散的驱动力 菲克第一定律告诉人们，浓度梯度是原子扩散的驱动力，原子从浓度高的区域流向浓度低的区域。浓度梯度消失后，系统趋于平衡，扩散应当停止。事实上，还存在溶质原子从低浓度区域流向高浓度区域的现象，例如，固溶体中发生的某些原子的偏聚和调幅分解。 从热力学来看，决定固溶体中扩散过程的驱动力不是浓度梯度，而是系统中组元的化学势梯度。在等温等压的条件下，不管浓度梯度如何，组元原子总是从化学势高的区域自发地转移到化学势低的区域，只有各组元的化学势在系统中的各点都相等时，才达到了平衡，宏观上不发生物质的转移。这样，菲克第一定律应当写成： （4－13） 式中 为扩散组元的化学势。 * Section 4.2 扩散的驱动力 （4－13）式称为菲克定律的普遍形式，负号表明，原子扩散的驱动力总是与化学位下降的方向一致，扩散朝着化学位减小的方向进行。 溶质原子从高浓度地区流向低浓度地区的扩散，称谓“下坡扩散”，扩散的结果使成分趋向于均匀，铸锭的均匀化退火就是这种形式的扩散。当浓度梯度方向与化学势梯度的方向相反时，溶质原子就会朝浓度梯度相反的方向迁移，即从低浓度区域流向高浓度区域，因为同类原子的聚集可显著地降低系统的自由能。例如，过饱和固溶体的分解过程。该扩散称为 “上坡扩散”，结果使合金趋向于分解为复相组织。 温度梯度、电场和局部应力状态也会影响扩散过程。 * * Figure Illustration of the concentration gradient * Section 4.4 Factors Affecting Diffusion Temperature and the Diffusion Coefficient (D) Types of Diffusion - volume diffusion, grain boundary diffusion, Surface