AKD-LT中性碱性造纸施胶剂的研制-南京林业大学学报.pdfVIP

第 23 卷第 1 期 南 京 林业大 学学 报 Vol. 23 No.1 1999 年 1 月 ]ournal of Nanjing Forestry University ]an. 1999 AKD-LT 中性/碱性造纸施胶剂的研制 戴红旗俞雪英吴佩琛毕松林 (南京林业大学制浆造纸研究所 南京 210037) 郑铁山 吕建明 (石家庄通力化工厂) 摘 要 系统分析和讨论了阳离子树脂型 AKD 施胶剂的制备工艺和影响乳液性能的多种因 素。发现AKD 乳化温度和时间、分散剂的选择和树脂的阳离子度对 AKD 胶的粒径、乳液稳 定性及施胶效能有较大的影响。结果表明树脂型 AKD 胶具有更高的阳电荷密度、更长的有 效贮存期和更好的施胶效能，且不易霉变。 关键词 阳离子树脂;AKD 乳液制备:造纸施胶剂 中图分类号 TS72 1. 5 Preparation of AKD-LT Neutral/ Alkaline Papermaking Sizing Agent Dai Hongqi Yu Xueying Wu Peichen Bi Songlin (Pupl and Paper Research Institute of Nanjing Forestry University Nanjing 210037) Zheng Tieshan Lü] ianming (Shijiazhuang Tongli Chemicals Factory) Abstract This paper systematically analyses the preparing technology of the cationic resin AKD size and the factors of the effecting AKD sizing efficency. It was found that the emulsifing temperature and time , the choice of the dispersants , and the charge density of the resin had a great effect on AKD quality. The re sult shows that the AKD size emulsified with cationic resin has higher charge density longer storage life and better sizing efficiency , and also no susceptibility to moulds. Key words Cationic resin; AKD emulsion preparation; Papermaking size 中性或碱性造纸取代松香 硫酸铝酸性造纸，可以提高纸的强度和纸的耐久性，增加填料用量，减 少细料的流失，节约能耗，从而降低生产成本。采用 AKD 中性施胶还可以降低系统对设备的腐蚀，提 高纸机臼水的封闭程度，减少废水排放量[1 ~7J 。目前，我国造纸工业由酸性造纸向中性造纸转换的一 个关键因素是提高国产 AKD 胶的质量和进一步降低 AKD 胶的生产成本。 目前西欧、北美中性纸和纸板的产量己超过 85% ， AKD 施胶剂己开发到第二代，乳液性能和施胶 收稿日期 1998-06 -18 修改稿收到日期 1999- 01 - 05 第一作者简介: 戴红旗，男，南京林业大学化学工