树脂整理亚麻织物舒适性能分析.docVIP

树脂整理亚麻织物舒适性能分析 　　摘要：本文分析了树脂整理对亚麻织物舒适性的影响，测试了树脂整理前后亚麻织物的弯曲应力应变性能、压缩性能、摩擦性能和透气透湿性能。结果表明：经树脂整理后，亚麻织物的力学性能、舒适性能发生明显改变。醚化DMDHEU树脂整理后的亚麻织物的综合服用性能优于DMDHEU树脂整理后的亚麻织物 关键词：亚麻；树脂整理；弯曲应力应变性能；压缩性能；透气透湿性能 中图分类号：TS197 文献标志码：A Analysis on the Comfort of Resin Finished Linen Fabric Abstract： The influences of resin finishing on the comfort of linen fabric were analyzed. The stress-strain properties， compressive properties， friction properties， air permeability and moisture permeability of pristine linen and finished linen were tested. The results showed that mechanical properties and comfort properties of linen fabrics changed obviously after resin finishing. The comprehensive properties of linen fabric finished by the etherified DMDHEU resin were better than that of linen fabric finished by DMDHEU resin. Key words： linen； resin finishing； stress-strain properties； compressive properties； friction properties 亚麻织物是一种性能优良的天然纤维素纤维织物，具有突出的吸湿、抗菌抑菌和卫生保健功能，为了使亚麻织物更好地服务于广大消费者，必须对其进行适当的功能整理。DMDHEU树脂具有免烫防缩功能，可以使织物达到防缩抗皱的效果。然而，经过树脂功能整理后的亚麻织物力学性能和穿着舒适性会受到不同程度的影响。本文主要研究树脂整理前后的亚麻织物的舒适性能和力学性能，讨论经树脂整理后亚麻织物的舒适性能变化情况 1 试验部分 1.1 材料和仪器 材料：亚麻织物（克重226 g/m2，齐齐哈尔金亚亚麻纺织有限公司）；DMDHEU树脂（自制），醚化DMDHEU树脂（醚化剂为1，4-丁二醇，自制），渗透剂JFC（西安润鑫化工科技有限公司），MgCl2（分析纯，潍坊市神州化学有限公司），柠檬酸（分析纯，苏州正洋化工科技有限公司） 仪器：YG821L型织物风格仪（莱州市电子仪器有限公司），YG461E-I型织物透气测试仪（温州际高检测仪器有限公司），YG（B）216-II型织物透湿量仪（温州大荣纺织仪器有限公司） 1.2 试验方法 整理液配方： （1）DMDHEU树脂整理液：DMDHEU?渲?90 g/L，渗透剂JFC 1.5 g/L， MgCl2 14 g/L （2）醚化DMDHEU树脂整理液：醚化DMDHEU树脂90 g/L，渗透剂JFC 1.5 g/L， MgCl2 14 g/L，柠檬酸1.5 g/L 整理工艺： 两浸两轧（25 ℃，轧余率100%）→ 预烘（80 ℃，3 min）→ 焙烘（160 ℃，3 min） 1.3 测试方法 （1）织物风格 依据FZ/T 01054.1 ～ 6 ― 1999《织物风格实验方法》，分别测试树脂整理前后亚麻织物对应的弯曲性能、压缩性能和摩擦性能 （2）透气性能 参照GB/T 5453 ― 1997《纺织品 织物透气性的测定》，测试单位时间内通过织物的空气流量体积 （3） 透湿性能 参照GB/T 12704.1 ― 2009《纺织品 织物透湿性试验方法 第 1 部分：吸湿法》，采用正杯法，在标准试验条件下，计算出树脂整理前后亚麻织物样品的透湿率（WVT）： 2 结果与讨论 树脂整理前后亚麻织物的舒适性性能，主要根据弯曲应力应变性能、压缩性能和摩擦性能进行分析和探究 2.1 应力应变性能 树脂整理前后，亚麻织物的弯曲应力应变性能如表1 所示 由表 1 可知，经醚化DMDHEU树脂整理的亚麻织物相比亚麻原织