汽动给水泵汽轮机叶片断裂机理分析.pdfVIP

材料热处理(12 ●失效分析● 汽动给水泵汽轮机叶片断裂机理分析 张 兵。郑准备。王小迎。温睿麟 (陕西电力科学研究院，陕西 西安710054) 摘 要：通过化学成分分析、宏观分析、显微组织分析、扫描电镜分析、能谱分析等方法。对某发电机组汽动 给水泵汽轮机断裂叶片进行了试验研究。结果表明，小汽轮机叶片为高周疲劳断裂失效。叶片塑性指标低和表面 加工精度差是导致开裂的重要原因。蒸汽腐蚀也加速了叶片的失效。 关键词：汽动给水泵；叶片；断裂机理；失效 中图分类号：TG167．2：TGl57 文献标识码：A 文章编号：1001．3814(2007)24．0073．03 Fracture Mechanism Analysis of Turbine Blades of Feedwater Pump Driven by Steam ZHANG Bing，ZHENG Zhun—bei，WANG Xiao—ying，WEN Rui—lin (Shaanxi Electric,~ower Research Institute，Xian 7 1 0054，China) Abstract：The facture mechanism of turbine blades of feedwater pump driven by steam have been studied by chemical elements analysis，macroscopical analysis，metallographic analysis，SEM analysis and EDS analysis．Th e resul~ show that the fracture invalidation of turbine blade is hi -frequency fatigue．Blade’S low plastic value and bad machining precision are major reason for fracture invalidation，steam erosion also speeds up the invalidation of turbine blades． Key words：feedwater pum p driven by steam；blade；fracture mechanism；invalidation 汽动给水泵可实现能量的梯级利用，降低能 两处断裂叶片的断裂位置均处在叶跟与叶面过渡 源消耗，提高机组热效率和经济效益[11。某发电厂 圆弧上方 15~20 mm内，断口垂直于叶片长度方 一 台引进330 MW发电机组采用汽动给水泵，汽 向，断VI表面已严重锈蚀(见图1)。断裂叶片两侧 动给水泵汽轮机(以下简称小汽轮机)为单缸、多 的叶片存在撞击痕迹和不同程度的变形．越靠近 级、冲动、凝汽式汽轮机，大轴轴径为225 nlIn，叶 断叶处的叶片变形越严重。宏观检查确认，有18 片分为八级，其中第五级叶片共计 100片。该机组 片叶片损伤严重，无法继续服役。 在运行48206．93 h后进行第二次大修时，检修人 员检查发现．小汽轮机转子第五级叶片断裂2片， 另有18片叶片存在不同程度的损伤。 1 现场检查及取样 1．1现场检查 小汽轮机转子第五级 2片断裂叶片间隔18 片叶片：两处断裂叶片的拉筋已全部破断，叶片断 图l叶片断口状况 裂部分连同破断的拉筋一同飞落，两处断裂叶片 Fig，1 Blade facture condition 的叶跟部分仍完好保留在轮缘上，未见松动现象。 1．2 取样情况