用聚乙烯醇改性合成酚脲醛呋喃树脂工艺研究.pdfVIP

材料与工艺 用聚乙烯醇改性合成酚脲醛呋喃树脂工艺研究 周利军，马 文 （宁夏共享化工有限公司,宁夏 银川 750021） 摘要：研究了用聚乙烯醇改性酚脲醛呋喃树脂的合成工艺。试验结果表明，经过改性的合成树 脂性能比较优良，其游离甲醛含量小于0.03％，抗拉强度达到了1.9 MPa。当加一定量的硅烷 （KH-602）时，该合成树脂的抗拉强度可达到2.2 MPa以上。 关键词：PVA；呋喃树脂；酚脲醛；强度；低甲醛 中图分类号：TG221 文献标识码：A 文章编号：1673-3320（2017）03-0037-04 Study on Technology Modifying Synthetic Urea-formaldehyde Resin by Polyvinyl Alcohol ZHOU Lijun,MA Wen (Kocel Chemicals. Co.,LTD.,Yinchuan 750021,Ningxia China) Abstract: A synthesis process whereby phenolic urea-formaldehyde resin was modified by polyvinyl alcohol was investigated. The results showed that the synthetic resin had better performance, its free formaldehyde content was less than 0.03%, and its the tensile strength reached 1.9 MPa. The addition of a certain amount of silane (KH-602) made the tensile strength of the synthetic resin reach as great as 2.2 MPa or more. Key words:polyvinyl alcohol; urea-formaldehyde; phenol-urea; strength; low formaldehyde 收稿日期：2017-03-14 作者简介：周利军（1994-），男，本科，从事呋喃树脂黏结剂的工作。 采用型内退火的办法来降低铸件残余应力， 成退火后再落砂，可以有效地避免铸件产生较大 不仅生产成本低，而且取消了退火环节，生产流 的残余应力，从源头上避免了产生较大的残余应 程更顺畅。所以，采用型内退火的方案来进行批 力。 量生产。从采用该工艺至今，已累计生产多个批 （4 ）传统退火方式为铸件落砂冷却后再采 次，近万件铸件，经检测，各批次铸件残余应力 用电炉加热的方式使铸件达到退火温度，耗能较 均满足技术要求。 高。采用型内退火工艺不存在二次加热，利用铸 件余温退火，节能环保。 5 结论 （1）由于高牌号缸盖材质要求高，铸件结构 参考文献: 复杂，采用传统退火的方式降低内应力时，必须 [1] 中国机械工程学会铸造分会. 铸造手册1[M]铸铁. 北京:机 保证充分的保温时间，尽可能多地释放内应力。 械工业出版社. 2003. [2] 吴德海, 钱立, 胡家骢. 灰铸铁球墨铸铁机器熔炼[M].北京: （2 ）采用退火方式消除铸件残余应力，冷却 中国水利水电出版社, 2006. 段温度梯度也是影响残余应