新型四酮染料在毛织物上染色及防紫外性能探究.doc

新型四酮染料在毛织物上染色及防紫外性能探究以指甲花醌为原料合成 3 只四酮染料，在弱酸性沸染条件下对羊毛的染色织物，干或湿摩擦牢度大部分在 4 ～ 5 级以上，除皂洗变色牢度相对较差外，毛沾色牢度和棉沾色牢度均在 4 级以上；日晒牢度均在 3 级左右；染色羊毛织物的紫外线防护系数UPF最高可达 174，长波紫外线透过率TUVA及中波紫外线透过率TUVB最低可分别达到 1.41% 及 0.38%。通过荧光光谱证实，3 只四酮染料具有吸收 290 ～ 400 nm波段紫外光、并将其转化为荧光的能力，为染料赋予羊毛织物显著的防紫外线性能提供了依据 On the condition of weak acid and over 95℃, wool fabrics were dyed with three tetrone dyes, which were synthesized by 2 ? hydroxyl - 1,4 - naphthoquinone. Dry and wet rubbing fastnesses of dyed wool fabrics were mostly above 4 ~ 5, except for poor discolor fastness to soap and light, the wool and cotton staining fastness were both above 4. The maximum ultraviolet protection factor(UPF) of dyed wool fabric was 174, and the minimum of TUVA and TUVB were respectively 1.41% and 0.38%. Confirmed by fluorescence spectra, the three tetrone dyes have abilities of absorbing 290 ~ 400 nm UV light and translating it into the fluorescence. It was concluded that synthetic dyes enable dyed wool fabrics with outstanding UV protection properties. 醌类化合物广泛存在于高等植物中，近年来，天然醌类优异的紫外吸收以及可见到近红外反射功能愈来愈引起人们的兴趣，这对纺织品防紫外功能整理具有重要启示。因此，本文重点研究了以指甲花醌为原料合成的四酮染料，对羊毛织物的染色及防紫外性能 1 实验部分 1.1 染化试剂及材料 羊毛织物（80S×80S）；化学试剂均为分析纯；染整助剂均为工业品；染料A1（4 ? 氯苯基）? 13 ? 苯基 ? 5H ? 二苯并?吨 ? 5，7，12，14（13H）? 四酮、A2（4 ? 羟基 ? 3 ? 甲氧基苯基）? 13 ? 苯基 ? 5H ? 二苯并?吨 ? 5，7，12，14（13H）? 四酮和A3（2 ? 羟基苯基）? 13 ? 苯基 ? 5H ? 二苯并?吨 ? 5，7，12，14（13H）? 四酮均由本课题组合成 1.2 直接染色工艺 羊毛织物 2.0 g，浴比 1∶40，染料 1.0%（o.w.f），将毛织物用沸水煮 15 min，冷却挤干水分，在 40 ℃入染，以 1 ℃/min升温至沸，染色 60 min，水洗，烘干。媒染浴比 1∶40，70 ℃时加入FeCl2 1.0%（o.w.f），以 1 ℃/min升温至 80 ℃或沸腾，媒染 45、60 min，水洗，烘干 1.3 性能测试 摩擦牢度、皂洗牢度和日晒牢度分别按 GB/T 3920 ― 1997、GB/T 3921.2 ― 1997和 GB/T 8426 ― 1998标准测试；防紫外性能按照澳大利亚/新西兰AS/NZS 4399标准测试；荧光光谱通过X荧光光谱仪EDX 3200S测定 2 结果与讨论 2.1 四酮染料的染色性能 由于四酮染料的染色机理与酸性染料相似,故选择在pH值 4.0 ～ 5.0 的弱酸性条件下对羊毛织物进行染色。从表 1、表 2 及表 3 中可以得出，染浴pH值为 4.0 时上染率较高，当pH值大于 4.0 时上染率呈现减小趋势；当pH值大于 4.0 时，染色样品K/S值呈现减小的趋势，说明染后织物的色深随着pH值的增大而变浅，其变化机理可能与四酮染料的结构有关，具体机理有待进一步研究 2.2 四酮染料的媒染性能 在pH值 4.0 的条件下，采用染料A1、A2对染色羊毛织物进行直接染色，再以Fe2+