铸态gh742 合金的凝固特点及枝晶偏析 - researchgate.pdf

See discussions, stats, and author profiles for this publication at: /publication/273204933 Solidification Characteristics and Dendritic Segregation of As-Cast GH742 Alloys Article in R RE MET L M TERI LS ND ENGINEERING · January 2010 CIT TIONS RE DS 3 35 7 authors, including: Xiaolin Pan Wenru Sun Northeastern University (Shenyang, China) Chinese cademy of Sciences 36 PUBLIC TIONS 68 CIT TIONS 60 PUBLIC TIONS 32 CIT TIONS SEE PROFILE SEE PROFILE Some of the authors of this publication are also working on these related projects: The precipitation activity of desilication products (DSPs) on stability of sodium aluminate solution View project ll content following this page was uploaded by Xiaolin Pan on 08 March 2015. The user has requested enhancement of the downloaded file. 第39 卷 第1 期 稀有金属材料与工程 Vol.39, No.1 2010 年 1 月 RARE METAL MATERIALS AND ENGINEERING January 2010 铸态 GH742 合金的凝固特点及枝晶偏析 1,2 2 3 2 2 1 2 潘晓林 ，孙文儒 ，李 战 ，杨树林 ，郭守仁 ，杨洪才 ，胡壮麒 (1. 东北大学，辽宁 沈阳 110004) (2. 中国科学院金属研究所，辽宁 沈阳 110016) (3. 沈阳理工大学，辽宁 沈阳 110168) 摘 要：高合金化GH742 合金存在严重的枝晶偏析，Nb 、Ti 大量偏聚于枝晶间，导致M C 碳化物、(γ+ γ′)共晶、Laves 相、δ相等析出；高Mo 含量及其枝晶间偏析是析出σ相的重要原因；La 、Ce 在枝晶间的富集促使含氧硫稀土相和Ni5Ce 相的析出。与一般合金凝固特点不同，高含量Al 、Ti 、Nb 导致GH742 合金凝固过程中先后发生(γ+ γ′)和(γ+Laves)两种 类型的共晶反应。结合差热分析技术和凝固组织特点确定了合金的凝固温度区间为 1346-1190 ℃，凝固顺序为γ、M C 、 (γ+ γ′) 、Laves 、Ni5Ce 。 关键词：GH742 ；凝固；偏析；组织 中图法分类