用粉煤灰及工业盐酸生产高效絮凝剂聚合氯化铝铁.docVIP

用粉煤灰及工业盐酸生产高效絮凝剂聚合氯化铝铁摘要: 利用粉煤灰和工业盐酸为主要原料,添加适量铝酸钙粉,制备出絮凝剂聚合氯化铝铁。对影响聚合氯化铝铁制备的因素,如粉煤灰的预处理温度、盐酸浓度、盐酸用量、反应温度和铝酸钙粉用量等进行了研究,得到了制备聚合氯化铝铁的优化条件,同时将该絮凝剂用于工业污水的处理。研究结果表明:制备的絮凝剂絮凝效果优于一些传统的絮凝剂;同时具有原料易得,制造成本低的优势。 关键词: 粉煤灰;工业盐酸;絮凝剂;聚合氯化铝铁;制备;污水处理 Abstract: A new type flocculant-polymeric aluminum ferric chloride was prepared. The main material was fly ash, and the other material was calcium aluminum. The effects of the optimum conditions were given in the experiment. The flocculating effect of the polymeric aluminum ferric chloride was researched in the treatment of practical industrial wastewater. Experimental results showed that the flocculating effect was superior to other traditional flocculants and has advantage of few dosage and quick sedimentation. It was a high effective flocculant. Key words: red mud; industrial hydrochloric acid; flocculant; polymeric aluminum ferric chloride; preparation; wastewater treatment 粉煤灰是发电厂最大的污染物,随着我国发电厂、城市供热工程不断增加,粉煤灰的产量也随之增多。以2006年的火电发电量计算,当年我国火电厂产生约2.4～2.9亿t粉煤灰和0.2～0.3亿t炉渣,居世界之首[1]。目前国内粉煤灰利用率只有30%～40%左右[2],发电厂大都将粉煤灰输送堆场堆存。粉煤灰堆存不但要占用大量的土地,污染环境,还使粉煤灰中的许多可利用成分得不到合理利用,造成资源浪费。因此对粉煤灰的综合利用是解决粉煤灰污染,实现循环经济的根本途径。 工业盐酸是硫基复合肥副产品,每生产1吨复合肥要副产0.3吨工业盐酸,对盐酸下游产品的开发也是解决工业盐酸出路,提高复合肥厂效益的有效途径。 聚合氯化铝铁是一种新型高效铝铁复合絮凝剂,该絮凝剂既有聚合铝盐基度高、对原水适应性强的特点,又有聚合铁密度大、絮体沉降快的优点[3]。它可克服铝盐处理后水样残余铝浓度高、沉降速度慢的不足,因此应用前景广阔。 本文利用粉煤灰中的残余的铝、铁制备一定铝铁比例的聚合氯化铝铁,实现资源的综合利用。将经过处理的粉煤灰与一定浓度的工业盐酸在一定的条件下反应制备铝铁的碱式盐,然后加入铝酸钙粉调节产品的盐基度和铝铁含量,得到一定碱化度和铝铁比的聚合氯化铝铁。 1 试验原料与方法 1.1 主要原料 基本原料:以山东某发电厂粉煤灰为基本原料,经分析其化学组成如下:Al2O3 23.76%,FeT9.52%,SiO2 58.06%,CaO 3.16%,其他5.50%。 其他原料:工业盐酸(公司副产品,浓度31%);铝酸钙粉(市售,Al2O3 含量53%) 1.2 主要仪器 722型分光光度计;JJ-4型电动搅拌机。 1.3 试验方法 1.3.1 聚合氯化铝铁的制备 将粉煤灰焙烧后研磨过120目筛。常压下,按一定配比将粉煤灰和一定浓度的工业盐酸加入带有回流冷凝管的四口烧瓶中,在一定温度下反应一定时间后,再加入适量铝酸钙粉,在一定温度下继续反应一定时间后,停止加热,陈化后得到深红棕色液体。 1.3.2 试验污水水质 污水取自某造纸厂污水,其具体水质指标见表1。 1.3.3 絮凝试验 取500mL污水于烧杯中,用盐酸或氢氧化钠溶液调节水样的pH值,加入一定量的絮凝剂,以350r/min快速搅拌2min,然后以80r/min慢速搅拌8 min,停止搅拌,静止沉降15min,在液面下2～3cm处取适量上清液,测定其COD值和浊度。 2 结果与讨论