Al、Cu含量对ZnAlCuMg合金性能的影响.pdfVIP

Vol-28No．6 铸造技术 Jun．2007 FOUNDRYTECHNoLoGY 刘洪军，李亚敏，郝 远 (兰州理工大学有色金属合金教育部重点实验室，甘肃兰州730050) 金力学性能和铸造流动性的影响。结果表明，铝含量从3％增加到14％，铜含量从3％增加到9％，合金力学性能明显增加，但铸 造流动性下降。综合考虑各种因素，得出新型模具锌合金的建议成分伽为：9％～11％～，7％～9％Cu，0．04％～O．05％Mg。 关键词：锌基模具舍金；A1舍量；Cu含量；性能 中图分类号：TG291文献标识码：A 文章编号：1000—8365(2007)06～0823—04 Effect0fAIandCuContenton of Al PropertiesZn-AI-Cu—Mgloy Yuan LIU un，LIYa-min，HAO Hong-j of of ofNon-ferrousMetal Education，Lanzhou (KeyLaboratory Alloys，TheMinistry UniversityTechnology， Lanzhou 730050，China) Cuis to anewZn—Ai- Abstract：Howtodetermineareasonable ofAIand a ingredient keydevelop mould with effectofAIandCucontentonmechanical Cu·Mg alloy highperformance．The and of mouldisstudied．The resultsshowthatthe fluidityZn．AI．Cu—Mgalloy experimental ofthe increases with thecontentsofAIandCufrom3％to propertiesalloy significantlyincreasing 14％and3％to the ofthe decreases．Itis thatthe 9％respectively．butfluidity alloy suggested reasonable is9—11wt％AI，7～9wt％Cuand composition 0．04～O．05wt％Mg． words：Zincbasedfor mould；AIcontent；Cu Key alloy content；Properties 锌基合金综合性能优良，作为模具材料，其快速经 性要优于刁相，所以锌合金的耐热性也随着铝含量的 济的制模特点，正适合于市场对多品种、小批量、价格 增加而提高。铜也是一种重要的合金元素，它的加入 低、生产周期短的塑料件的需求。在实际应用中也取 可以提高锌基模具合金的力学强度和耐热耐磨性。通 得了良好的社会效益与经济效益。但是这种模具材料