掺合料对硫铝酸盐水泥抗Cl^-渗透性能的影响.pdfVIP

2008．No．1 T 一7一 掺合料对硫铝酸盐水泥抗Cl一渗透性能的影响 张云飞 ，张德成 一，杜纪锋 ，程 新 (1．济南大学 材料学院，山东 济南 250022；2．武汉理工大学，湖北 武汉 430070) 摘要：研究了矿渣、粉煤灰和沸石粉单掺及复掺时对硫铝酸盐水泥砂浆Cl渗透性的影响，采用SEM、孔结构等方法分 析了不同龄期的净浆水化产物。结果表明，在硫铝酸盐水泥浆体中，加入掺合料可以改善结构致密性，提高抗Cl一渗透能 力，3种掺合料作用效果为：矿渣粉煤灰沸石粉；复掺时效果更好，矿渣与粉煤灰复掺矿渣与沸石粉复掺沸石粉与 粉煤灰复掺。 关键词：矿渣；粉煤灰；沸石粉；硫铝酸盐水泥；CI渗透性 Abstract：The chloride permeability of sulphoaluminate cement paste could be changed by the addition of GGBFS．fly ash． zeolite either respectively or compositely．Their hydration products had been studied by means of SEM and pore structure at different curing age．The results showed that the addition of blending materials could improve the compactibility of cement paste structure，then increased anti-chloride permeability．The effect of slag was best and zeolite was worst；It could get a better effect when the blending materials were composited，and the composite admixture of slag and fly ash was the most， that of zeolite and fly ash was the least． Key words：GGBFS；fly ash；zeolite；sulph0aluminate；chloride permeability First author s address：School of Materials Science and Engineering of Jinan University，Jinan 250022，Shandong，China 中图分类号：TQ172．746 文献标识码：A 文章编号：1002—9877(2008)ol一0007—03 0 引言 表1 原材料的化学成分 ％ 硫铝酸盐水泥以其早强、高强、高抗渗、高抗冻、 品种 Loss CaO SiO2 A12O3 F02O3 MgO Na2O K2O SO3 P1O5 耐蚀和低碱度等特点在工程中得到广泛应用，特别是 硫铝酸盐 0 水泥 ．O9 45．25 10．96 28．93 3．7l 1．45 8．88 在冬季施工、水工工程和修补工程等特殊工程中应 用，更发挥出了其优良的性能。但在硫铝酸盐水泥中 矿渣 1．17 35-41 32-32 12．02 6-25 8．14 0-23 0．16 掺入不同性能的掺合料对其性能的影响，目前研究的 粉煤灰 2．56 2．57 54．0 27．7 6．1l l-23 0-37 1．50 0．14 较少。水泥中使用的掺合料种类主要有：粉煤灰、矿 沸石粉 2．43 1-42 72．o9