放电等离子烧结与传统烧结法制备( ba, sr) tio3 陶瓷的 - 材料工程.pdfVIP

( Ba, Sr) T iO 3 65 ( Ba, Sr) TiO 3 Comparison Betw een Spark Plasma Sintering and Convent ional Sintering of ( Ba, Sr) T iO3 Ceramics , ( , 43007 ) ZHU Kan, CHEN Wan-ping ( Department of Physics, Wuhan U niversity, Wuhan 43007 , China) : ( Spark Plasma Sintering, SPS) , ( Ba, Sr) TiO 3 ( 1 00~ 1300 e ) , ( Ba, Sr) TiO , 3 SPS ( Ba, Sr) T iO , , SEM SPS 3 , 1 40e SPS ( Ba, Sr) T iO 3 : ( SPS) ; ( Ba, Sr) TiO ; 3 : TB3 1 : A : 1001-4381( 008) 10-0 65-03 Abstract : ( Ba, Sr) T iO3 pow ders w ere synthetic in both Spark Plasma Sintering( SPS) method and con- ventional method at the temperature 1 00-1300 e , respectively. T he result revealed that the sample w hich prepared in SPS method w as alw ays has a higher dielectric constant w ith a relatively low dielec- tric loss at a specific temperature. Also the SEM photos show ed the densification of ceramic surface could be improved through the rapid sintering of SPS. Moreover , w e observed that 1 40 e is the best temperature for sintering after w e tried several others. Key words: spark plasma sintering; ( Ba, Sr) T iO3 ceramic; de