混凝土早龄期抗裂性能测试方法评述全文译文概要1.docVIP

Review on Testing Method of Cracking Resistance Performance of Concrete at Early Age Zhifang Zhao1, Xiaojie Feng1, Zhigang Zhao2, Liang Wang1 1. College of Civil Engineering and Architecture, Zhejiang University of Technology, Hangzhou, Zhejiang 310014, P. R. China. 2. School of electron and Information, Zhejiang University of Media and Communications，Hangzhou, Zhejiang 310018, P. R. China. 3. Zhejiang Provincial Key Laboratory of Hydraulic Disaster Prevention and Mitigation，Hangzhou, Zhejiang 310020, P. R. China. ABSTRACT Cracking of concrete at early age arises from volume changes such as drying shrinkage, autogenous shrinkage, plastic shrinkage and thermal deformation. These volume changes cause tensile stresses in the material when they are restrained. So it is necessary to study the testing and evaluation method of cracking resistance performance of concrete at early age. Some substantial achievements have been made in the field of research on cracking resistance performance of concrete at early age. Some testing methods such as slab test, ring specimen test, elliptical ring specimen test and uniaxial restraint test are comparative maturity methods to test the cracking resistance performance of concrete at early-age. The testing and evaluation method of cracking resistance performance of concrete at early age need to be further studied with the development of sustainable concrete materials. This paper focuses on the current testing methods of cracking resistance performance of concrete at early age and gives introduction and review on them. KEYWORDS Concrete；Volume changes ；Restraint；Early age；Cracking resistance performance 0 Introduction Concrete often cracks due to the gradual extension of the common visible and invisible cracks, which results in gradual structure deterioration, eventually leading to structural failures or damage thus shortening the service life【1、2】invasion of hazardous substances in the structure environment, thereby cause