热镀锌钢丝生产线的改造.pdfVIP

第34卷 第l期 金 属 制 品 2008年 2月 V0L 34 No．1 Stee】 Wire Products Februam 2008 热镀锌钢丝生产线的改造 张建强 曹德润 (天津市环钟钢丝有限公司 300400) 摘 要 从收放线装置、预处理_[艺、锌锅加热方式、抹拭及冷却系统等方面对进口Galfan镀层生产线进行技术改 造。改造后，镀锌钢丝产量、综合力学性能、表面质量大大提高，材料及能源消耗大大降低，并减少了废液排放，改 善了作业环境。 关键词 Gaifan镀层生产线；预处理_r艺；抹拭系统；技术改进 中图分类号 TG356．27 Alteration of Production Line for Hot Dipping Galvanizing Steel Wire Zhang Jianqiang Cao Derun (Huanzhong Steel Wire Co．，Ltd．ofTianjin City 300400) Abstract To carry through technology alteration for the imported Galfan coating production line from such aspects as take— up and pay—off，pre—treatment process，heating mode of zinc pot，l ab and cooling system．After alteration，the output of galvanizing steel wire，synthetical mechanical property and the su~aee quality are raised greatly，the consumptions of mate— rial and energy are cut down，and the letting of waster liquid decrease，working environment is improved． Keywords Galfan coating production line；pre—treatment process；rub system；technologyalteration 1 问题的提出 线，钢丝在高速运行中时松时紧、易甩圈、颤动、张力 天津市环钟钢丝有限公司1998年引进美国24 不均匀，从而影响钢丝镀层的均匀性及质量。 头Galfan镀层生产线。该生产线用于生产01．8～ (2)钢丝运行。钢丝通过各工艺槽时，由于采 5．0 mm镀层钢丝，设计伪值120～150 mm·m／rain， 用转动式通轴压线，钢丝在运行过程中频繁改变运 年生产能力20 000 t。设备安装后试车时发现钢丝 行方向，运行阻力比较大，同时也会造成钢丝颤动。 镀层表面存在锌瘤且镀层厚度波动较大， 值也很 (3)镀前清洗。由于速度较高，镀前清洗效果 难达到设计要求。1998年12月一2006年对Galfan 不佳，从而导致钢丝漏镀。 镀槽的钢丝抹拭设备进行了大量的探索，使用了固 (4)烘干能力。钢丝出助镀槽后烘干能力不 体、气体、固体+气体等多种抹拭方法，产品镀层质 足，钢丝表面存有少量未烘干的氯化铵，在进入锌锅 量有一定改善，但仍较难控制，造成批量生产时质量 瞬问，未烘干的氯化铵遇高温急剧膨胀，直至爆破， 不稳定，生产能力受到很大制约。 其爆破力导致锌液面波动和钢丝抖动，从而造成钢 为此天津市环钟钢丝有限公司2006年对