车用铅蓄电池极板腐蚀变形的处理及预防 Treatment and prevention of corrosion and deformation of the lead-acid battery plate.pdfVIP

电池工业 车用铅蓄电池极板腐蚀变形的处理及预防 李婷 (风神汽车修理厂，湖北武汉430055) 摘要：正极板栅的腐蚀变形程度是铅蓄电池老化程度最主要的标志。介绍了极板板栅腐蚀和变形的 特征；极板板栅的腐蚀和变形机理和正极板板栅腐蚀和变形的原因分析，以及正极板板栅腐蚀和变 形的消除方法；同时指出了正极板板栅腐蚀和变形的预防和补救措施。 关键词：铅蓄电池；极板；腐蚀变形；处理及预防 中图分类号：TM912．1文献标志码：A 文章编号：1008-7923(2010)02-0116—04 Treatmentand ofcorrosionanddeformationofthe prevention lead-acid batteryplate LITing Mowr (FengshenRepairFactory,形妇Hubei430055,China) Abstract：The corrosionanddeformationoflead-acidarean of positive酊d battery importantsign corrosionanddeformationcharacteristicsof oflead-acidweredescribed aging．The positivegids battery inthis mechanismandcausestothecorrosionanddeformationwere the paper．The analyzed．And methodstodiminatethecorrosionanddeformationof oflead-acidwere positivegdds battery introduced．Italso outthe measuresandremedialactions． pointed preventing words：lead-acid and and Key corrosion；treatment battery；plates；deformation prevention 铅蓄电池是由正负极板、隔板、壳体、电解液和 因为栅架上的锑会污染负极板上的海绵状纯铅，减 接线桩头等组成，其放电的化学反应是依靠正极板 弱了完全充电后蓄电池内的反电动势，造成水的过 活性物质(二氧化铅和铅)和负极板活性物质(海绵状 度分解，大量氧气和氢气分别从正、负极板上逸出， 纯铅)在电解液(稀硫酸溶液)的作用下进行。其中极板 使电解液减少。用钙代替锑，就可以改变完全充电后 的栅架，传统蓄电池用铅锑合金制造，免维护蓄电池 的蓄电池的反电动势，减少过充电流，降低液体气化 是用铅钙合金制造。不同的材料就会产生不同的现 速度，从而减低了电解液的损失。在蓄电池的充电过 象：传统蓄电池在使用过程中会发生减液现象，这是 程中，板栅都会被氧化成硫酸铅和二氧化铅，最后导 致丧失支