高聚物乳液基酚醛树脂粉玻化微珠复合保温浆料的研制 李聚刚 （苏州市建筑科学研究院，江苏 苏州 215129 ） 摘要：本文通过试验，考察了乳液种类及用量、玻化微珠的级配和用量、酚醛树脂粉的 用量、疏水剂的种类和用量对产品抗压强度、压剪粘结强度、软化系数、导热系数、吸水率 等性能的影响规律，研制出一种用于外墙外保温用高聚物乳液基酚醛树脂粉玻化微珠复合保 温浆料。本产品克服了常用有机、无机保温材料的缺点，具有燃烧性能好、导热系数低、吸 水率低等特点，并且生产工艺和施工工艺简单，造价成本低的优点。 关键词：外墙外保温；玻化微珠、酚醛树脂粉、燃烧性能、导热系数 Preparation of polymer emulsion based phenolic resin powder glass bead composite insulation slurryLI Jugang （Suzhou institute of building research,Jiangsu,suhzou,215129） Abstract:Through the experiment, the emulsion type and amount, glass beads, gradation and amount of phenolic resin powder dosage, hydrophobic agent types and dosage on the compressive strength, shear strength, softening coefficient, thermal conductivity, water absorption properties of law, developed a used for exterior wall external thermal insulation glazed hollow bead phenolic resin powder composite thermal insulation mortar. The product overcomes the common organic, inorganic heat preservation material weaknesses, combustion performance is good, low thermal conductivity, low water absorption, and simple production process and construction technology, the advantages of low manufacturing cost. Keywords: Exterior insulation; glass beads, phenolic resin powder, combustion performance, thermal conductivity 0 引言 建筑节能是关系到可持续发展的一个重大课题，在建筑领域研究开发并且推广应用新型 建筑节能环保材料是建筑领域节能减排降耗的关键。目前建筑外墙外保温用的保温材料按材 质可以分为有机保温材料和无机保温材料。有机保温材料主要有模塑聚苯乙烯泡沫塑料板 （EPS ）、挤塑聚苯乙烯泡沫板（XPS ）、硬质聚氨酯发泡板（PU ）、酚醛泡沫板（PF ）等， 无机保温材料主要有岩棉板、玻璃棉、膨胀珍珠岩、硅酸钙板、泡沫玻璃板、发泡水泥板等。 模塑聚苯乙烯泡沫塑料板（EPS ）和挤塑聚苯乙烯泡沫板（XPS ）尤其是挤塑聚苯乙烯泡沫 板（XPS ），隔热保温性能优异、施工工艺成熟，在2013 年初公安部“65 号文件”取消之 后，以砂浆涂覆的挤塑聚苯乙烯泡沫板（XPS ）复合板成了市场的主流。但是用于挤塑聚苯 乙烯泡沫板（XPS ）发泡的主要发泡剂HCFC22 和HCFC2142b 是两种严重消耗臭氧的物质， 大量使用引起很强的温室效应，因此面对严重的环境压力。硬质聚氨酯发泡板价格一直居高 不下，难以大范围推广。酚醛泡沫板也由于密度大、整体强度低、国内产品质量参差不齐， 短期内无法成为主流产品。无机类保温材料不存在防火安全问题，但是普遍存在强度低、整 体性差、吸水率高等缺点。至于曾经大量使用的