浮法 英文（Float in English）.doc

浮法 英文（Float in English） 2.2 strengthen the wall of cooling pond and chest wall As late kiln burning loss and operation are partial material, the material of wall brick has been washed before and after the thin, breast wall brick end was burn out how the hook or clearance brick through the fire, make it face under the support of the iron and tower plate due to the lack of protection and direct exposure to the furnace flame, if improper handling time. Probably because of iron parts (slap iron, iron plate) burning kiln body deformation caused serious, eventually led to the small furnace crib and breast wall slope collapse and cannot be redeemed. Use the fan blowing to protect the traditional operating method of iron parts, although can properly reduce the temperature of burning area, ease the sustained high temperature to increase the risk of loss, but, in the late kiln using loss serious critical moment, the general cooling wind blowing protection schemes in this to no avail. So used in the erection of the gaps of the wall on both sides of compressed air piping, and prepare the duck bill directly high pressure cooling compressed air nozzle, pressure maintain at about 2 mpa, to block further burning flame iron; At the same time, a few rows of 160 x 40 x 40 (mm) T - shaped water bags are installed on the tray, and the water pressure is maintained at about 1MPa, which is forced to cool the area. The enhanced dual cooling protection measures effectively reduced the loss of the site. The refractory brick will be eroded, thinned and perforated after long use. If happens dont take measures, the molten glass occurs leakage, the flame out of accident, and around the steel structure will be damaged by high temperature, once the steel structure bear the refractory furnace will result in danger of collapse. The wall tiles of the melting section The wall brick of the wall, especially in the 1 ~ 5P area, will be greatly eroded by the wall tiles near the molten glass surface. In ord