焊条温度（The electrode temperature）.docVIP

焊条温度（The electrode temperature） The welding rod tends to deteriorate the process performance due to the moisture absorption, resulting in the instability of the arc and the increase of spatter, and it is easy to produce the defects such as stoma and crack. Therefore, the electrode must be dried strictly before use. General acid electrode drying temperature 150-200 ℃, 0.5 1 hour; Alkaline electrode drying temperature 350-400 ℃, 1 -- 2 hours time, after drying in the 100-150 ℃ heat preservation box, along with it. JB4709 has recommended temperature and temperature (non-mandatory), but it is best to refer to the temperature and time requirements of the electrode warranty. You said J427 belongs to alkaline welding rod, the temperature at 350 ℃, insulation 1 h. What is the difference between electrode J422 and J427? J422 - - acid electrode GB model E4303 Structural steel welding rod, metal tensile strength of weld metal not less than 420Mpa, titanium oxide type coating, ac and dc, mainly used for welding low carbon steel and strength grade low alloy steel such as 09Mn2, etc. J427 - - alkaline welding rod GB model E4315 Structural steel welding rod, weld metal tensile strength not less than 420Mpa, low hydrogen sodium type drug skin, dc reverse connection, mainly used for welding important low carbon steel and low alloy steel such as 09MnSi. 20G steel welding material Welding materials for 20g steel flange of 20g steel tube of low pressure vessel, welding material for steel structure of no.20 steel structure, and welding materials for 20g steel welding 20g steel. Some of you are eager to ask the question: The material thickness is: Flange thickness 38 steel pipe wall thickness 15 Flange thickness 28 steel pipe wall thickness 10 The best answer I think electrode arc welding with J426 (model E4316), J427 (model for E4315) electrode is better. Because it is JB/T 4709-2000 steel pressure vessel welding procedures recommended selection of welding material. J422 is an acid elec