梯度硬质合金涂层基体的制备（Preparation of substrate of gradient cemented carbide coating）.docVIP

梯度硬质合金涂层基体的制备（Preparation of substrate of gradient cemented carbide coating） Cemented carbide as a kind of tool material, because of its high hardness, high strength, high modulus of elasticity, wear resistance and corrosion resistance, such as performance, has been widely used in all kinds of cutting tools, mining tools and wear-resisting corrosion resistant parts. In order to adapt to a variety of service conditions, improve efficiency, in view of the traditional carbide exists the contradiction of high hardness and toughness of low, people have developed such as gradient cemented carbide, ultrafine cemented carbide materials. In recent years, with the concept of functional gradient materials, the functional gradient cemented carbide is becoming one of the important research contents in the field of hard alloy. In order to improve the cutting performance and service life of carbide cutting tools, thin layer and high hardness wear-resisting material can be applied on the surface of alloy. Due to different thermal expansion coefficients of different materials, the coating material may crack during cooling process due to thermal stress. Because of the brittleness of coating materials, cracks are usually more easily produced on the surface of the coating and extended to the substrate. As much as possible in order to prevent the material failure due to crack propagation, and is helpful to obtain high performance cemented carbide cutting tool material, gradient on matrix for processing, make the carbide formed in the substrate surface area lack of cubic phase and the toughness of carbon nitride area, the area of binder content higher than that of the matrix in the name of the binder content. When coating formed in the crack extension to the region, due to its good toughness, can absorb energy, crack propagation and can effectively prevent the crack to expand alloy inside, improve the usability of cemented carbide cutting tools This paper mainly reviews the preparation o